High-pressure trans...
High-pressure transformations of NbO2F
-
- Carlson, Stefan (författare)
- Lund University,Lunds universitet,MAX IV-laboratoriet,MAX IV Laboratory,European Synchrotron Radiation Facility
-
- Larsson, Ann Kristin (författare)
- Stockholm University
-
- Rohrer, Franziska E. (författare)
- Stockholm University
-
(creator_code:org_t)
- 2000
- 2000
- Engelska 8 s.
-
Ingår i: Acta Crystallographica. Section B: Structural Science. - 0108-7681. ; 56:2, s. 189-196
- Relaterad länk:
-
https://lup.lub.lu.s...
Abstract
Ämnesord
Stäng
- The ReO3-type structure NbO2F, niobium dioxyfluoride, has been studied at high pressures using diamond anvil cells and synchrotron X-ray radiation. High-pressure powder diffraction measurements have been performed up to 40.1 GPa. A phase transition from the cubic (Pm3m) ambient pressure structure to a rhombohedral (R3c) structure at 0.47 GPa has been observed. Rietveld refinements at 1.38, 1.96, 3.20, 6.23, 9.00 and 10.5 GPa showed that the transition involves an a-a-a- tilting of the cation-anion coordination octahedra and a change of the anion-anion arrangement to approach hexagonal close packing. Compression and distortion of the Nb(O/F)6 octahedra is also revealed by the Rietveld refinements. At 17-18 GPa, the diffraction pattern disappears and the structure becomes X-ray amorphous.