Nano-Scratching resistance of high-chromium white cast iron and its correlation with wear of cBN tool in machining
-
- Chen, L. (författare)
- Sichuan University
-
- Persson, J. (författare)
- Lund University,Lunds universitet,Industriell Produktion,Institutionen för maskinvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Production and Materials Engineering,Department of Mechanical Engineering Sciences,Departments at LTH,Faculty of Engineering, LTH
-
- Ståhl, J. E. (författare)
- Lund University,Lunds universitet,Industriell Produktion,Institutionen för maskinvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Production and Materials Engineering,Department of Mechanical Engineering Sciences,Departments at LTH,Faculty of Engineering, LTH
-
visa fler...
-
- Zhou, J. M. (författare)
- Lund University,Lunds universitet,Industriell Produktion,Institutionen för maskinvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Production and Materials Engineering,Department of Mechanical Engineering Sciences,Departments at LTH,Faculty of Engineering, LTH
-
visa färre...
-
(creator_code:org_t)
- 2017
- 2017
- Engelska 8 s.
-
Ingår i: Journal of Superhard Materials. - 1063-4576. ; 39:5, s. 365-372
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://lup.lub.lu.s...
-
https://doi.org/10.3...
-
visa färre...
Abstract
Ämnesord
Stäng
- In this paper, a nano-scratch testing approach was used to measure and evaluate the abrasion wear resistance of high-chromium white cast irons in order to understand the wear mechanism in the interaction between the high-chromium white cast iron and the cBN cutting tool during the machining process. Scratch testing was performed on a nanoindentation instrument using a diamond indenter as the scratch tool. Linear multi-pass scratches in the same path were made on pre-worn surfaces of test materials. The correlation of the scratching resistance and tool wear measured from the machining is presented by the flank wear and maximum scratch depth. The appearance of the cutting edge on a cBN tool suggests that the abrasion wear is mainly related with a combined effect of the carbides and the matrix during machining the high-chromium white cast iron.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Maskinteknik -- Tribologi (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Mechanical Engineering -- Tribology (hsv//eng)
Nyckelord
- cBN
- fracture
- high-chromium cast iron
- scratch test
- wear mechanism