Norberg, Stefan,1972Chalmers tekniska högskola,Chalmers University of Technology
(författare)
Cation movement and phase transitions in KTP isostructures; X-ray study of sodium-doped KTP at 10.5 K
- Artikel/kapitelEngelska2003
Förlag, utgivningsår, omfång ...
Nummerbeteckningar
-
LIBRIS-ID:oai:research.chalmers.se:04b7a626-e881-4944-aea6-b2d1ddeb8bab
-
https://research.chalmers.se/publication/97683URI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:art swepub-publicationtype
-
Ämneskategori:ref swepub-contenttype
Anmärkningar
-
An accurate structure model of sodium-doped potassium titanyl phosphate, (Na0.114K0.886) K(TiO)(2)(PO4)(2), has been determined at 10.5 K by single-crystal X-ray diffraction. In addition to the low-temperature data, X-ray intensities have been collected at room temperature. When the temperature was decreased from room temperature to 10.5 K, both potassium cations moved 0.033 (2) Angstrom along the c-axis, i.e. in the polar direction within the rigid Ti-O-P network. This alkaline metal ion displacement can be related to the Abrahams-Jamieson-Kurtz T-C criteria for oxygen framework ferroelectrics. Potassium titanyl phosphate (KTP) is a well known material for second harmonic generation (SHG), and the influence of sodium dopant on the TiO6 octahedral geometry and SHG is discussed. The material studied crystallizes in the space group Pna2(1) with Z = 4, a = 12.7919 (5), b = 6.3798 (4), c = 10.5880 (7) Angstrom, V = 864.08 (9) Angstrom(3), T = 10.5 (3) K and R = 0.023.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Sobolev, Alexander
(författare)
-
Streltsov, Victor
(författare)
-
Chalmers tekniska högskola
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Acta Crystallographica Section B: Structural Science59:3, s. 353-3600108-76811600-5740
Internetlänk
Hitta via bibliotek
Till lärosätets databas