A detailed microstructural and corrosion analysis of magnesium alloy WE43 manufactured by selective laser melting
-
- Esmaily, M. (författare)
- Massachusetts Institute of Technology (MIT),Monash University
-
- Zeng, Z. (författare)
- Monash University
-
- Mortazavi, Anna, 1986 (författare)
- Harvard University,Monash University
-
visa fler...
-
- Gullino, A. (författare)
- Monash University,Politecnico di Torino,Polytechnic University of Turin
-
- Choudhary, S. (författare)
- Monash University
-
Derra, T. (författare)
-
Benn, F. (författare)
-
D'Elia, F. (författare)
-
Müther, M. (författare)
-
- Thomas, S. (författare)
- Monash University
-
- Huang, A. (författare)
- Monash University
-
- Allanore, A. (författare)
- Massachusetts Institute of Technology (MIT)
-
Kopp, A. (författare)
-
- Birbilis, Nick (författare)
- Australian National University
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2020
- 2020
- Engelska.
-
Ingår i: Additive Manufacturing. - : Elsevier BV. - 2214-8604. ; 35
- Relaterad länk:
-
https://doi.org/10.1...
-
visa fler...
-
https://research.cha...
-
visa färre...
Abstract
Ämnesord
Stäng
- The production of magnesium alloy WE43 was achieved by selective laser melting (SLM). The alloy was investigated after SLM, hot isostatic pressing (HIP), and solutionising heat treatment. The microstructure and corrosion behaviour of the specimens were carefully characterised, whilst assessed and contrast relative to the conventionally cast alloy counterpart. The SLM prepared specimens possess a unique microstructure comprising fine grains growing with a strong [0001] texture along the building direction with a low fraction of process-induced and metallurgical defects, reaching < 0.1 %, after optimising the SLM parameters and the HIP treatment. Electrochemical measurements demonstrated that the SLM prepared WE43 is cathodically more active as compared with its cast counterpart. It is proposed that this behaviour is due to a high density of zirconium-rich oxide particles uniformly distributed throughout the alloy microstructure as well as the alterations in the chemical composition of the solid-solution matrix originating from the high cooling rates of SLM. It was also noted that the oxide particles are mainly sourced by powder. The present results suggest that the corrosion of SLM prepared Mg alloys could be greatly improved once the influence of powder characteristics is further understood and controlled.
Ämnesord
- NATURVETENSKAP -- Kemi -- Annan kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Other Chemistry Topics (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik -- Korrosionsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering -- Corrosion Engineering (hsv//eng)
Nyckelord
- Selective laser meltingMagnesium alloyWE43CorrosionMicrostructure
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Esmaily, M.
-
Zeng, Z.
-
Mortazavi, Anna, ...
-
Gullino, A.
-
Choudhary, S.
-
Derra, T.
-
visa fler...
-
Benn, F.
-
D'Elia, F.
-
Müther, M.
-
Thomas, S.
-
Huang, A.
-
Allanore, A.
-
Kopp, A.
-
Birbilis, Nick
-
visa färre...
- Om ämnet
-
- NATURVETENSKAP
-
NATURVETENSKAP
-
och Kemi
-
och Annan kemi
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Materialteknik
-
och Metallurgi och m ...
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Kemiteknik
-
och Korrosionsteknik
- Artiklar i publikationen
-
Additive Manufac ...
- Av lärosätet
-
Chalmers tekniska högskola