High-Temperature Corrosion of HVAF-Sprayed Ni-Based Coatings for Boiler Applications

• The present study investigates the initial corrosion behaviour of HVAF-sprayed NiCr, NiAl and NiCrAlY coatings in two different environments, O 2 + H 2 O and O 2 + H 2 O + KCl at 600 °C for up to 168 h in order to evaluate the possibility of utilizing such coatings in biomass- and waste-fired boilers. SEM/EDX analysis showed that all coatings displayed a protective behaviour in O 2 + H 2 O. Upon addition of KCl (O 2 + H 2 O + KCl), the corrosion behaviour of the NiCr coating drastically changed as it formed a thick oxide layer and displayed major chlorine diffusion down to the substrate. The NiCrAlY coating displayed a significantly better corrosion resistance with only minor oxide formation. The NiAl coating exhibited a protective behaviour similar to when exposed in the absence of KCl indicating that a thin protective oxide has formed on the coating surface. The performance of the NiAl and NiCrAlY coatings is promising for future studies with long-term exposures in more corrosive environments such as in a biomass- and waste-fired boiler.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Medicinteknik -- Medicinsk material- och protesteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Medical Engineering -- Medical Materials (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik -- Korrosionsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering -- Corrosion Engineering (hsv//eng)

Nyckelord

HVAF

KCl-induced corrosion

Ni-based coatings

Waste

Biomass

Manufacturing and materials engineering

Publikations- och innehållstyp

art (ämneskategori)

ref (ämneskategori)