Effect of Cr3C2 Content on the Microstructure and Wear Resistance of Fe3Al/Cr3C2 Composites
-
- Feng, Yingkai (författare)
- Tsinghua University
-
Shan, Jiguo (författare)
-
- Zhao, L. (författare)
- China Iron and Steel Research Institute Group
-
visa fler...
-
- Liu, Zhenbo (författare)
- China Iron and Steel Research Institute Group
-
- Gong, Karin Anne Xia, 1965 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Li, Changhai, 1941 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa färre...
-
(creator_code:org_t)
- 2022-12-17
- 2022
- Engelska.
-
Ingår i: Coatings. - : MDPI AG. - 2079-6412. ; 12:12
- Relaterad länk:
-
https://research.cha... (primary) (free)
-
visa fler...
-
https://research.cha...
-
https://doi.org/10.3...
-
visa färre...
Abstract
Ämnesord
Stäng
- In this paper, an engine piston ring coating comprising composite material of Fe3Al and Cr3C2 mixed powder was prepared by laser cladding onto carbon structural steel. The microstructure and tribological properties of the cladding materials were investigated through X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), transmission electron microscopy (TEM), and wear tests. The influence mechanism of the Cr3C2 content in cladding powder was studied. During the process of wear, the soft Fe3Al/Fe2AlCr matrix is first ground off, and the hard Cr7C3 phase initially supports the abrasive surface before being worn away into hard particles, resulting in abrasive wear. With the increase in Cr3C2 content, the hardness of the cladding layer increases, the proportion of the Cr7C3 phase increases, and the morphology changes from a sparse network to a dense floccule. Of the cladding layers with different Cr3C2 content, the 15 wt.% Cr3C2 cladding layer had the lowest friction coefficient, and the 25 wt.% Cr3C2 cladding layer had the lowest wear rate. The low wear rate of the 25 wt.% Cr3C2 cladding layer can be attributed to the fact that adhesive wear does not easily occur and the fine microstructure of the strengthening phase, which facilitates better separation in the grinding surfaces.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Maskinteknik -- Tribologi (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Mechanical Engineering -- Tribology (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
- NATURVETENSKAP -- Kemi -- Materialkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Materials Chemistry (hsv//eng)
Nyckelord
- wear resistance
- laser cladding
- carbide behavior
- Fe Al/Cr C composites 3 3 2
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
-
Coatings
(Sök värdpublikationen i LIBRIS)
Till lärosätets databas