Gejke, Cecilia,1973Chalmers tekniska högskola,Chalmers University of Technology
(författare)
Structural investigation of the Li+ ion insertion/extraction mechanism in Sn-based composite oxide glasses
- Artikel/kapitelEngelska2001
Förlag, utgivningsår, omfång ...
Nummerbeteckningar
-
LIBRIS-ID:oai:research.chalmers.se:3eb14ecc-e428-4f46-9adf-f77e2a5a5b78
-
https://research.chalmers.se/publication/40693URI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:art swepub-publicationtype
-
Ämneskategori:ref swepub-contenttype
Anmärkningar
-
The effect of lithium insertion for two Sn-based composite oxide glasses, Sn2BPO6 and Sn2P2O7, was examined during the first electrochemical discharge/charge cycle. Electrodes based on these glasses were analysed with micro-Raman spectroscopy at different steps during the cycle. In-situ X-ray diffraction has been used to confirm the amorphous state during the lithium insertion and extraction process. No alloy formation between Li and Sn could be discerned throughout the first cycle. It was found that when lithium enters the electrode, a reaction at the surface of the glass particles takes place resulting in Li3PO4, Li2O and SnO2 formation. The charge compensation mechanism is thought to be the reduction of Sn2+ to Sn. The formation of Li3PO4 is found to be irreversible and is as such partly responsible for the large observed capacity loss during the first cycle.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Zanghellini, Ezio,1962Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)zanghell
(författare)
-
Börjesson, Lars,1957Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)lborje
(författare)
-
Fransson, L.
(författare)
-
Edström, K.
(författare)
-
Chalmers tekniska högskola
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Journal of Physics and Chemistry of Solids62, s. 1213-1218.0022-3697
Internetlänk
Hitta via bibliotek
Till lärosätets databas