Effect of different solution heat treatments on hot ductility of superalloys Part 2-Allvac 718Plus
-
- Andersson, Joel Håkan, 1981 (författare)
- Högskolan Väst,Avd för tillverkningsprocesser,Department of Materials Technology, Volvo Aero Corporation, Trollhättan, Sweden and Department of Materials and Manufacturing Technology, Chalmers University of Technology, Gothenburg, Sweden,PTW
-
- Sjöberg, Göran, 1946 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology,Department of Materials Technology, Volvo Aero Corporation, Trollhättan, Sweden and Department of Materials and Manufacturing Technology, Chalmers University of Technology, Gothenburg, Sweden
-
- Viskari, Leif, 1982 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology,Department of Applied Physics, Chalmers University of Technology, Gothenburg, Sweden
-
visa fler...
-
- Chaturvedi, Mahesh (författare)
- University of Manitoba,Department of Mechanical and Industrial Engineering, University of Manitoba, Winnipeg, MB, Canada
-
visa färre...
-
(creator_code:org_t)
- Taylor & Francis Group, 2012
- 2012
- Engelska.
-
Ingår i: Materials Science and Technology. - : Taylor & Francis Group. - 1743-2847 .- 0267-0836. ; 28:6, s. 733-741
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://research.cha...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- The hot ductility of Allvac 718Plus for different solution heat treatments (954 degrees C-15 h, 954 degrees C-1 h, 982 degrees C-1 h and 1050 degrees C-3 h+954 degrees C-1 h) has been investigated using Gleeble testing. Substantial variations in the microstructure among the heat treatments affected the Gleeble test hot ductility only to a very limited extent. Constitutional liquation of the NbC phase was found to be the main cause for the poor ductility at high testing temperatures in the on-heating cycle as well as at the lower temperatures on-cooling. Grain boundary delta phase was seen to assist the constitutional liquation of the NbC phase. Based on established evaluation criteria for Gleeble ductility testing, a ranked indicator for weldability is suggested.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Nyckelord
- allvac 718plus
- Weldability
- waspaloy
- Hot ductility
- alloy 718
- inconel
- weldability
- precipitation
- Allvac 718Plus
- Gleeble testing
- cracking
- Manufacturing and materials engineering
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas