Characterization of pack cemented Ni(2)Al(3 )coating exposed to KCl(s) induced corrosion at 600 degrees C
-
- Dahl, K. V. (författare)
- Danmarks Tekniske Universitet,Technical University of Denmark
-
- Slomian, Andreas, 1989 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Lomholt, T. N. (författare)
- Danmarks Tekniske Universitet,Technical University of Denmark,FORCE Technology
-
visa fler...
-
- Kiamehr, S. (författare)
- Danmarks Tekniske Universitet,Technical University of Denmark
-
- Grumsen, F. B. (författare)
- Danmarks Tekniske Universitet,Technical University of Denmark
-
- Montgomery, M. (författare)
- Danmarks Tekniske Universitet,Technical University of Denmark
-
- Jonsson, Torbjörn, 1970 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa färre...
-
(creator_code:org_t)
- 2017-10-26
- 2018
- Engelska.
-
Ingår i: Materials at High Temperatures. - : Informa UK Limited. - 0960-3409 .- 1878-6413. ; 35:1-3, s. 267-274
- Relaterad länk:
-
https://backend.orbi...
-
visa fler...
-
https://research.cha...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Oxidation of Ni2Al3 produced by pack aluminizing of pure nickel was studied with and without 0.10 mg cm(-2) KCl(s) deposit in an environment containing 5% O-2, 40% H2O and 55% N-2 at 600 degrees C for up to 168 h. Oxide microstructure and composition was investigated by SEM/EDX, BIB, TEM and GDOES. Oxidised Ni2Al3 shows minimal weight gain, while adding KCl results in a small weight loss consistent with evaporation of KCl. On the surface of samples exposed to the gas environment only, a 30 nm oxide of Al oxide was present, but where KCl was present as deposit, 50-250 nm thick nodules form that are enriched in K, O and Al.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
- NATURVETENSKAP -- Kemi -- Materialkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Materials Chemistry (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik -- Korrosionsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering -- Corrosion Engineering (hsv//eng)
Nyckelord
- KCl
- Nickel aluminide
- high temperature corrosion
- electron microscopy
- 600 degrees C