Nanometer-thick films of titanium oxide acting as electrolyte in the polymer electrolyte fuel cell
-
- Ekström, Henrik (författare)
- KTH,Tillämpad elektrokemi
-
- Wickman, Björn, 1980 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology,Chalmers tekniska högskola, Göteborg
-
- Gustavsson, Marie, 1969 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology,Chalmers tekniska högskola, Göteborg
-
visa fler...
-
- Hanarp, Per, 1974 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology,Chalmers tekniska högskola, Göteborg
-
- Eurenius, Lisa, 1977 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology,Chalmers tekniska högskola, Göteborg
-
- Olsson, Eva, 1960 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology,Chalmers tekniska högskola, Göteborg
-
- Lindbergh, Göran (författare)
- KTH,Tillämpad elektrokemi
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2007
- 2007
- Engelska.
-
Ingår i: Electrochimica Acta. - : Elsevier BV. - 0013-4686 .- 1873-3859. ; 52:12, s. 4239-4245
- Relaterad länk:
-
https://research.cha...
-
visa fler...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- 0–18 nm-thick titanium, zirconium and tantalum oxide films are thermally evaporated on Nafion 117 membranes, and used as thin spacer electrolyte layers between the Nafion and a 3 nm Pt catalyst film. Electrochemical characterisation of the films in terms of oxygen reduction activity, high frequency impedance and cyclic voltammetry in nitrogen is performed in a fuel cell at 80 ◦C and full humidification. Titanium oxide films with thicknesses up to 18 nm are shown to conduct protons, whereas zirconium oxide and tantalum oxide block proton transport already at a thickness of 1.5 nm. The performance for oxygen reduction is higher for a bi-layered film of 3 nm platinum on 1.5 or 18 nm titanium oxide, than for a pure 3 nm platinum film with no spacer layer. The improvement in oxygen reduction performance is ascribed to a higher active surface area of platinum, i.e. no beneficial effect of combining platinum with zirconium, tantalum or titanium oxides on the intrinsic oxygen reduction activityis seen. The results suggest that TiO2 may be used as electrolyte in fuel cell electrodes, and that low-temperature proton exchange fuel cells could be possible using TiO2 as electrolyte.
Ämnesord
- NATURVETENSKAP -- Kemi -- Oorganisk kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Inorganic Chemistry (hsv//eng)
Nyckelord
- Oxygen reduction
- Titanium oxide
- Proton conduction
- Fuel cell
- Thermal evaporation
- Electrochemistry
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Ekström, Henrik
-
Wickman, Björn, ...
-
Gustavsson, Mari ...
-
Hanarp, Per, 197 ...
-
Eurenius, Lisa, ...
-
Olsson, Eva, 196 ...
-
visa fler...
-
Lindbergh, Göran
-
visa färre...
- Om ämnet
-
- NATURVETENSKAP
-
NATURVETENSKAP
-
och Kemi
-
och Oorganisk kemi
- Artiklar i publikationen
-
Electrochimica A ...
- Av lärosätet
-
Chalmers tekniska högskola
-
Kungliga Tekniska Högskolan