Influence of firing conditions and production methods on fracture strength of titanium-based metal ceramic crowns

Artikel/kapitelEngelska2018

Förlag, utgivningsår, omfång ...

2017-07-20
Informa UK Limited,2018

Nummerbeteckningar

LIBRIS-ID:oai:research.chalmers.se:6d7d54b1-a295-46c1-afed-1dc2fc71b90b
https://research.chalmers.se/publication/501741URI
https://research.chalmers.se/publication/502786URI
https://doi.org/10.1080/01694243.2017.1352119DOI
https://urn.kb.se/resolve?urn=urn:nbn:se:mau:diva-5965URI

Kompletterande språkuppgifter

Språk:engelska
Sammanfattning på:engelska

Ingår i deldatabas

SwePubSwePub

Klassifikation

Ämneskategori:art swepub-publicationtype
Ämneskategori:ref swepub-contenttype

Anmärkningar

Objectives: This study evaluated the effect of argon atmosphere compared with vacuum during porcelain firing on the fracture strength of crowns made of porcelain and electron beam melted (EBM) Ti-6Al-4 V, cast commercially pure titanium or milled commercially pure titanium. Methods: Sixty crown copings of c. p. titanium, Ti-6Al-4 V alloy and porcelain were fabricated using three production techniques. The copings were fired either under vacuum or in an argon gas atmosphere. Specimens were subdivided into groups of cast c. p. titanium, milled c. p. titanium and EBM Ti-6Al-4 V which were further subdivided according to firing modes employing either vacuum or argon gas. The 60 specimens were subjected to cyclic preloading and thermocycling, and were then individually loaded until interface fractured. Differences between the group mean values were calculated using the one-way ANOVA and Tukey's range test. Two fractured samples from each group were cut with a diamond blade and examined using SEM and EDS for visualization and chemical composition analysis of the fractured interface. Results: The highest mean fracture strength values, though not significant, were recorded for the groups fired in argon atmosphere, and the lowest mean fracture strength values were recorded for the groups fired in vacuum, with one exception. Comparing the two main groups of firing atmosphere, no significant difference could be documented. SEM and EDS analysis indicated clear differences in composition and structure between the groups included in the study. Conclusions: Firing in argon atmosphere does not significantly improve the fracture strength of porcelain bonded to titanium.

Ämnesord och genrebeteckningar

MEDICIN OCH HÄLSOVETENSKAP Hälsovetenskap Sjukgymnastik hsv//swe
MEDICAL AND HEALTH SCIENCES Health Sciences Physiotherapy hsv//eng
TEKNIK OCH TEKNOLOGIER Materialteknik Annan materialteknik hsv//swe
ENGINEERING AND TECHNOLOGY Materials Engineering Other Materials Engineering hsv//eng
TEKNIK OCH TEKNOLOGIER Medicinteknik Medicinsk material- och protesteknik hsv//swe
ENGINEERING AND TECHNOLOGY Medical Engineering Medical Materials hsv//eng
argon
bond strength
dental ceramics
Titanium
dental porcelain

Biuppslag (personer, institutioner, konferenser, titlar ...)

Khan, F. (författare)
Andersson, Martin,1974Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)martina (författare)
Vult von Steyern, PerMalmö universitet,Odontologiska fakulteten (OD)(Swepub:mau)odpevu (författare)
Malmö universitetOdontologiska fakulteten (OD) (creator_code:org_t)

Sammanhörande titlar

Ingår i:Journal of Adhesion Science and Technology: Informa UK Limited32:3, s. 225-2380169-42431568-5616

Internetlänk

Hitta via bibliotek

Journal of Adhesion Science and Technology (Sök värdpublikationen i LIBRIS)

Till lärosätets databas

1 av 1
Föregående post
Nästa post
Till träfflistan

Hitta mer i SwePub

Av författaren/redakt...: Haag, P.; Khan, F.; Andersson, Marti ...; Vult von Steyern ...

Om ämnet

MEDICIN OCH HÄLSOVETENSKAP: MEDICIN OCH HÄLS ...; och Hälsovetenskap; och Sjukgymnastik

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Annan materialte ...

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Medicinteknik; och Medicinsk materi ...

Artiklar i publikationen: Journal of Adhes ...

Av lärosätet: Chalmers tekniska högskola; Malmö universitet

Sök utanför SwePub

Sök vidare i:: Google; Google Book Search; Google Scholar

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

LIBRIS.kb.se