Low-frequency and microwave performances of laser-ablated epitaxialNa 0.5 K 0.5 NbO 3 films on high-resistivitySiO 2 /Si substrates
-
- Abadei, Saeed, 1961 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Gevorgian, Spartak, 1948 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
Grishin, Alex (författare)
-
(creator_code:org_t)
- AIP Publishing, 2002
- 2002
- Engelska.
-
Ingår i: Journal of Applied Physics. - : AIP Publishing. - 0021-8979 .- 1089-7550. ; 91, s. 2267-
- Relaterad länk:
-
https://research.cha...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- The dielectric properties of laser-ablated 0.5-μm-thick c-axis epitaxialNa 0.5 K 0.5 NbO 3 (NKN) films on high-resistivity (>7.7 kΩ cm) siliconSiO 2 /Si substrates are studied experimentally in the temperature interval of 30–320 K and at frequencies of 1.0 MHz–40 GHz. The films are grown by laser ablation from a stoichiometric target. For the measurements, planar 0.5-μm-thick gold electrodes (interdigital and straight slot) are photolithography defined on the top surface of NKN films. The slot width between the electrodes is 2.0 or 4.0 μm. At low frequencies(f 1. At microwave frequencies(f>10 GHz), the voltage dependence of the capacitance is given by the NKN film. More than a 13% capacitance change at 40 V dc bias and a Q factor of more than 15 are observed at 40 GHz, which make the structure useful for applications in electrically tunable millimeter-wave devices
Ämnesord
- NATURVETENSKAP -- Fysik -- Den kondenserade materiens fysik (hsv//swe)
- NATURAL SCIENCES -- Physical Sciences -- Condensed Matter Physics (hsv//eng)
Nyckelord
- Dielectric thin films
- Capacitance
- Electrical resistivity
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas