Heat-Affected-Zone Liquation Cracking in Welded Cast Haynes® 282®

• Varestraint weldability testing and Gleeble thermomechanical simulation of the newly developed cast form of Haynes® 282® were performed to understand how heat-affected-zone (HAZ) liquation cracking is influenced by different preweld heat treatments. In contrast to common understanding, cracking susceptibility did not improve with a higher degree of homogenization achieved at a higher heat-treatment temperature. Heat treatments with a 4 h dwell time at 1120 °C and 1160 °C exhibited low cracking sensitivity, whereas by increasing the temperature to 1190 °C, the cracking was exacerbated. Nanosecond ion mass spectrometry analysis was done to characterize B segregation at grain boundaries that the 1190 °C heat treatment indicated to be liberated from the dissolution of C–B rich precipitates.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Maskinteknik -- Energiteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Mechanical Engineering -- Energy Engineering (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Annan materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Other Materials Engineering (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)

Nyckelord

Gleeble

boron

nanoSIMS

Varestraint

cracking

Haynes® 282®

Publikations- och innehållstyp

art (ämneskategori)

ref (ämneskategori)