Alumina scale formation on a powder metallurgical FeCrAl alloy (Kanthal APMT) at 900-1100°C in dry O2 and in O2 + H2O
-
- Engkvist, Josefin, 1972 (författare)
- Högskolan Dalarna,Materialvetenskap
-
- Canovic, Sead, 1979 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Hellström, Kristina M, 1971 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa fler...
-
- Järdnäs, Anders, 1969 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Svensson, Jan-Erik, 1965 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Johansson, Lars-Gunnar, 1952 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Olsson, Mikael (författare)
- Högskolan Dalarna,Materialvetenskap
-
- Halvarsson, Mats, 1965 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa färre...
-
(creator_code:org_t)
- 2009-09-25
- 2010
- Engelska.
-
Ingår i: Oxidation of Metals. - : Springer Science and Business Media LLC. - 1573-4889 .- 0030-770X. ; 73:1, s. 233-253
- Relaterad länk:
-
https://doi.org/10.1...
-
visa fler...
-
https://research.cha...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- A Rapidly Solidified Powder (RSP) metallurgical FeCrAl alloy, Kanthal APMT, was exposed in dry and humid O-2 for 72 h at 900-1,100 A degrees C. The formed oxide scales were characterized using gravimetry in combination with advanced analysis techniques (SEM, EDX, TEM, XRD, AES and SIMS). The oxide scales were at all exposures composed of two-layered alpha-Al2O3 scales exhibiting a top layer of equiaxed grains and a bottom layer containing elongated grains. A Cr-rich zone, originating in the native oxide present before exposure, separated these two layers. The top alpha-Al2O3 layer is suggested to have formed by transformation of outwardly grown metastable alumina, while the inward-grown bottom alpha-Al2O3 layer had incorporated small Zr-, Hf- and Ti-rich oxide particles present in the alloy matrix. The scale also contained larger Y-rich oxide particles. Furthermore, in the temperature range studied, the presence of water vapour accelerated alloy oxidation somewhat and affected scale morphology.
Ämnesord
- NATURVETENSKAP -- Kemi -- Oorganisk kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Inorganic Chemistry (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Annan teknik -- Övrig annan teknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Other Engineering and Technologies -- Other Engineering and Technologies not elsewhere specified (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Nyckelord
- Oxidation
- FeCrAl
- Water vapour
- Alumina
- Steel Forming and Surface Engineering
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Engkvist, Josefi ...
-
Canovic, Sead, 1 ...
-
Hellström, Krist ...
-
Järdnäs, Anders, ...
-
Svensson, Jan-Er ...
-
Johansson, Lars- ...
-
visa fler...
-
Olsson, Mikael
-
Halvarsson, Mats ...
-
visa färre...
- Om ämnet
-
- NATURVETENSKAP
-
NATURVETENSKAP
-
och Kemi
-
och Oorganisk kemi
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Annan teknik
-
och Övrig annan tekn ...
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Materialteknik
-
och Metallurgi och m ...
- Artiklar i publikationen
-
Oxidation of Met ...
- Av lärosätet
-
Chalmers tekniska högskola
-
Högskolan Dalarna