Investigation of Homogenization and its Influence on the Repair Welding of Cast Allvac 718Plus
-
- Andersson, Joel Håkan, 1981 (författare)
- Högskolan Väst,Avd för tillverkningsprocesser,Volvo Aero Corporation, Materials Technology Department, Trollhättan, Sweden och Chalmers University of Technology, Department of Materials and Manufacturing Technology, Göteborg,Sweden,PTW
-
- Sjöberg, Göran, 1946 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology,Volvo Aero Corporation, Materials Technology Department, Trollhättan, Sweden och Chalmers University of Technology, Department of Materials and Manufacturing Technology, Göteborg, Sweden
-
- Larsson, Josefine (författare)
- Chalmers tekniska högskola,Chalmers University of Technology,Chalmers University of Technology, Department of Materials and Manufacturing Technology, Göteborg,Sweden
-
(creator_code:org_t)
- ISBN 9781617827709
- 2012-08-17
- 2010
- Engelska.
-
Ingår i: Proceedings of The 7th International Symposium on Superalloy 718 and Derivatives, TMS (The Minerals, Metals and Materials Society). - Hoboken, NJ, USA : John Wiley & Sons, Inc.. - 9781617827709 ; 1, s. 439-454, s. 439-454
- Relaterad länk:
-
https://doi.org/10.1...
-
visa fler...
-
https://research.cha...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- Heat treatment experiments have been carried out to bring understanding to the efficacy of different temperatures and dwell times on the degree of homogenization of the cast Allvac 718Plus alloy which is prone to segregation mainly due to its high content of niobium. The effect of homogenization on weld repair was also examined. The homogenization heat treatment temperatures ranged from 1050°C to 1200°C with 1hr, 5 hrs and 10 hrs dwell times. The degree of homogenization was measured as the reduction of the amount of Laves phase by manual point counting in an optical microscope at high magnification. Longer range, interdendritic, patterns were established through line scan EDS analysis in SEM. It was found that short time (1hr) does not significantly reduce the amount of Laves phase whereas 5 hrs and 10hrs are much more efficient. Interdendritic homogenization does not occur to any measurable extent even at the highest temperature and longest dwell time (1200°C-10hrs) which was also reflected in bulk macro Vickers hardness tests.In the weld repair tests, one of the most homogenized material conditions (1125°C-5hrs +1200°C-10hrs) turned out to be the most prone to cracking while the number of weld cracks after a moderate homogenization heat treatment (1125°C-5hrs) was much smaller .
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Nyckelord
- casting
- Allvac 718Plus
- welding
- homogenization
- Produktions- och materialteknik