Comparative study for selective lithium recovery via chemical transformations during incineration and dynamic pyrolysis of EV li-ion batteries
-
- Balachandran, Srija (författare)
- KTH,Resursåtervinning,Kungliga Tekniska Högskolan (KTH),Royal Institute of Technology (KTH)
-
- Forsberg, Kerstin, 1979- (författare)
- KTH,Resursåtervinning,Kungliga Tekniska Högskolan (KTH),Royal Institute of Technology (KTH)
-
- Lemaitre, Tom, 1995 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology,Department of Chemistry and Chemical Engineering, Industrial Materials Recycling and Nuclear Chemistry, Chalmers University of Technology
-
visa fler...
-
- Vieceli, Nathalia Cristine, 1989 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology,Department of Chemistry and Chemical Engineering, Industrial Materials Recycling and Nuclear Chemistry, Chalmers University of Technology
-
- Lombardo, Gabriele, 1990 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology,Department of Chemistry and Chemical Engineering, Industrial Materials Recycling and Nuclear Chemistry, Chalmers University of Technology
-
- Petranikova, Martina, 1983 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology,Department of Chemistry and Chemical Engineering, Industrial Materials Recycling and Nuclear Chemistry, Chalmers University of Technology
-
visa färre...
-
(creator_code:org_t)
- 2021-08-04
- 2021
- Engelska.
-
Ingår i: Metals. - : MDPI AG. - 2075-4701. ; 11:8
- Relaterad länk:
-
https://research.cha... (primary) (free)
-
visa fler...
-
https://www.mdpi.com...
-
https://doi.org/10.3...
-
https://doi.org/10.3...
-
https://research.cha...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- Selective leaching of Li from spent LIBs thermally pretreated by pyrolysis and incineration between 400 and 700 °C for 30, 60, and 90 min followed by water leaching at high temperature and high L/S ratio was examined. During the thermal pretreatment Li2CO3 and LiF were leached. Along with Li salts, AlF3 was also found to be leached with an efficiency not higher than 3.5%. The time of thermal pretreatment did not have a significant effect on Li leaching efficiency. The leaching efficiency of Li was higher with a higher L/S ratio. At a higher leaching temperature (80 °C), the leaching of Li was higher due to an increase in the solubility of present Li salts. The highest Li leaching efficiency of nearly 60% was observed from the sample pyrolyzed at 700 °C for 60 min under the leaching condition L/S ratio of 20:1 mL g−1 at 80 °C for 3 h. Furthermore, the use of an excess of 10% of carbon in a form of graphite during the thermal treatment did not improve the leaching efficiency of Li.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik -- Kemiska processer (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering -- Chemical Process Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik -- Polymerteknologi (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering -- Polymer Technologies (hsv//eng)
- NATURVETENSKAP -- Kemi -- Materialkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Materials Chemistry (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering (hsv//eng)
Nyckelord
- Incinera-tion
- Li-ion batteries
- Electric vehicles
- Water leaching
- Pyrolysis
- A combined method of recycling
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
-
Metals
(Sök värdpublikationen i LIBRIS)
Till lärosätets databas