1. |
- Jiang, Liang, et al.
(author)
-
Formation of Spinel Phases in Oxidized BOF Slag under Different Cooling Conditions
- 2017
-
In: Steel Research International. - : John Wiley & Sons. - 1611-3683 .- 1869-344X. ; 88:11
-
Journal article (peer-reviewed)abstract
- To enhance utilization of wastes generated from steelmaking, a BOF slag sample from Ning Steel group in China is treated by oxidizing at 1500 °C for 30 min and then cooled by different methods. The treated samples are characterized, in combination with calculations using FactSage 6.4. XRD results show that iron oxides in BOF slag are converted largely by the oxidation to spinel phases, Fe3O4 and MgFe2O4, which also eliminates free CaO and MgO. EDS analyses show Fe element existing in di-calcium silicate and glass phase, which are Fe3+ ions formed by oxidation. An incorporation of Fe3+ ions into crystal structures has stabilized high temperature polymorph of C2S, β-C2S, and α’-C2S, in the treated slag samples. Fe3+ ions may also act as a network former to facilitate glass formation. This may make it possible for the glass and α’-C2S phase to complement each other, leading to a higher hydraulicity, while the BOF slag, after the spinel separation, is blended in cements. Some suggestions are proposed, based on the present and early studies, to enhance hydraulicity for the BOF slag, as well as grain sizes of spinel phases, which may result in economic and environmental benefits for steel and cement industries.
|
|
2. |
- Jiang, Liang, et al.
(author)
-
Structural Characteristics and Hydration Kinetics of Oxidized Steel Slag in a CaO-FeO-SiO2-MgO System
- 2019
-
In: High Temperature Materials and Processes. - : Walter de Gruyter. - 0334-6455 .- 2191-0324. ; 38:1, s. 290-300
-
Journal article (peer-reviewed)abstract
- Although steel slag exhibits cementitious properties, the addition of steel slag in cement is still limited due to both the presence of excess iron oxides and instability of free lime and periclase. This paper proposes a method for oxidizing molten slag in air, aiming at extraction of superfluous wustite and stabilization of free lime and periclase. Mineralogical characteristics of raw slag and modified products were examined using X-ray diffraction (XRD), scanning electron microscopy equipped with backscattered electron imaging (SEM-BEI), energy dispersive spectrometry (EDS) and thermogravimetric analysis (TGA) with differential scanning calorimetry (DSC). Thermodynamic calculations were performed to aid to discuss the experimental results. The results indicate that non-magnetic wustite and periclase are transformed into magnetic spinel (magnetite/magnesioferrite) after oxidation. Temperature has a significant effect on the formation of spinel. The mass fraction of free lime decreases from 3.54 wt.% to 0.96 wt.% as a result of the conversion from free lime to calcium ferrite.
|
|