1. |
- Reichel, L., et al.
(author)
-
Increased magnetocrystalline anisotropy in epitaxial Fe-Co-C thin films with spontaneous strain
- 2014
-
In: Journal of Applied Physics. - : AIP Publishing. - 0021-8979 .- 1089-7550. ; 116:21, s. 213901-
-
Journal article (other academic/artistic)abstract
- Rare earth free alloys are in focus of permanent magnet research since the accessibility of the elements needed for nowadays conventional magnets is limited. Tetragonally strained iron-cobalt (Fe-Co) has attracted large interest as promising candidate due to theoretical calculations. In experiments, however, the applied strain quickly relaxes with increasing film thickness and hampers stabilization of a strong magnetocrys- talline anisotropy. In our study we show that already 2 at% of carbon substantially reduce the lattice relaxation leading to the formation of a spontaneously strained phase with 3% tetragonal distortion. In these strained (Fe0.4Co0.6)0.98C0.02 films, a magnetocrystalline anisotropy above 0.4 MJ/m3 is observed while the large polarization of 2.1 T is maintained. Compared to binary Fe-Co this is a remarkable improve- ment of the intrinsic magnetic properties. In this paper, we relate our experimental work to theoretical studies of strained Fe-Co-C and find a very good agreement.
|
|
2. |
- Salikhov, R., et al.
(author)
-
Enhanced spin-orbit coupling in tetragonally strained Fe-Co-B films
- 2017
-
In: Journal of Physics. - : Institute of Physics Publishing (IOPP). - 0953-8984 .- 1361-648X. ; 29:27
-
Journal article (peer-reviewed)abstract
- Tetragonally strained interstitial Fe-Co-B alloys were synthesized as epitaxial films grown on a 20 nm thick Au0.55Cu0.45 buffer layer. Different ratios of the perpendicular to in-plane lattice constant c/a = 1.013, 1.034 and 1.02 were stabilized by adding interstitial boron with different concentrations 0, 4, and 10 at.%, respectively. Using ferromagnetic resonance (FMR) and x-ray magnetic circular dichroism (XMCD) we found that the total orbital magnetic moment significantly increases with increasing c/a ratio, indicating that reduced crystal symmetry and interstitial B leads to a noticeable enhancement of the effect of spin-orbit coupling (SOC) in the Fe-Co-B alloys. First-principles calculations reveal that the increase in orbital magnetic moment mainly originates from B impurities in octahedral position and the reduced symmetry around B atoms. These findings offer the possibility to enhance SOC phenomena - namely the magnetocrystalline anisotropy and the orbital moment - by stabilizing anisotropic strain by doping 4 at.% B. Results on the influence of B doping on the Fe-Co film microstructure, their coercive field and magnetic relaxation are also presented.
|
|