1. |
- Arasteh, Rouhollah, et al.
(author)
-
Effects of Fiber Spinning on the Morphology, Rheology, Thermal, and Mechanical Properties of Poly(trimethylene terephthalate)/Poly(ethylene terephthalate) Blends
- 2014
-
In: Advances in Polymer Technology. - : Wiley. - 0730-6679 .- 1098-2329. ; 33:S1, s. 21443-
-
Journal article (peer-reviewed)abstract
- The morphology, thermal behavior, rheological, and mechanical properties of poly(trimethylene terephthalate) (PTT)/poly(ethylene terephthalate) (PET) blend fibers were investigated. The scanning electron microscopy studies revealed the formation of a microfibrillar network of the PET within the PTT matrix after the fiber-spinning process. Differential scanning calorimetry results demonstrated that although the thermal characteristics of the amorphous phase were unaffected by the fiber-spinning process, the melting and crystallization behavior of the blends was altered by the elongation flow imposed during the melt spinning. The viscoelastic behavior of the PTT/PET blends was also studied by a steady shear rate and dynamic sweep rheological experiments before and after the spinning process. The induced morphology and crystallization reordering resulting from the fibrillation process are shown to have a remarkable effect on the complex viscosity profile of the PTT/PET fibers, particularly in the blend containing 30 wt% PET. The mechanical testing showed that tenacity and Young's modulus of the PTT fibers increased with the addition of PET up to 30 wt%.
|
|
2. |
- Kaptan, Navid, et al.
(author)
-
Thermal Behavior and Degradation Kinetics of Compatibilized Metallocene-Linear Low Density Polyethylene/Nanoclay Nanocomposites
- 2014
-
In: Polymer-plastics technology and engineering (Softcover ed.). - : Informa UK Limited. - 0360-2559 .- 1525-6111. ; 53:9, s. 890-902
-
Journal article (peer-reviewed)abstract
- Morphology, thermal degradation and kinetics of metallocene-linear-low-density polyethylene (m-LLDPE)/m-LLDPE-graft-maleic anhydride (m-LLDPE-g-MA)/nanoclay nanocomposites were compared with m-LLDPE/nanoclay, m-LLDPE-g-MA/nanoclay and m-LLDPE/m-LLDPE-g-MA systems. X-ray diffraction measurements revealed intercalated and "highly intercalated'' morphologies for the nanocomposites. Thermogravimetric analysis demonstrated that although thermal degradation of m-LLDPE systems were delayed upon the inclusion of nanoclay in air, an inverse effect was perceived for the nanoclay under inert atmosphere. This conclusion was supported by kinetic analysis in terms of reaction order and activation energy. The results obtained from kinetics models also put forward the contribution of m-LLDPE-g-MA, as a compatibilizer, to the thermal stability enhancement through intermolecular cross-linking augmentation.
|
|