| 1. |
- Du, Yong, et al.
(author)
-
Flexible ternary carbon black/Bi2Te3 based alloy/polylactic acid thermoelectric composites fabricated by additive manufacturing
- 2020
-
In: Journal of Materiomics. - : ELSEVIER. - 2352-8478 .- 2352-8486. ; 6:2, s. 293-299
-
Journal article (peer-reviewed)abstract
- Flexible ternary carbon black/Bi2Te3 based alloy/polylactic acid (CB/BTBA/PLA) composites were fabricated by additive manufacturing and their thermoelectric properties were investigated from 300 K to 360 K. At 300 K, as the mass ratios of BTBAs in the composites increased from 38.5% to 71.4%, both the electrical conductivity and Seebeck coefficient of the composites increased from 5.8 S/cm to 13.3 S/cm, and from 60.2 mV/K to 119.9 mV/K, respectively, and the thermal conductivity slightly increased from 0.15 W m(-1)K(-1) to 0.25 W m(-1)K(-1), as a result, the ZT value of the composites increased from 0.004 to 0.023. As the temperature increased from 300 K to 360 K, the electrical conductivity of all the composites slightly decreased, while the thermal conductivity slowly increased, and a highest ZT value of 0.024 was achieved for the composites with 71.4% BTBAs at 320 K. Unlike traditional sterolithography, fused deposition modeling, selective laser melting, etc., this additive manufacturing process can directly print the solutions which contain inorganic fillers and polymer matrixes into almost any designed intricate geometries of thermoelectric composites, therefore this process has great potential to be used for fabrication of flexible polymer based thermoelectric composites and devices. (C) 2020 The Chinese Ceramic Society. Production and hosting by Elsevier B.V.
|
|
| 2. |
- Du, Yong, et al.
(author)
-
Flexible Thermoelectric Double-Layer Inorganic/Organic Composites Synthesized by Additive Manufacturing
- 2020
-
In: Advanced Electronic Materials. - : WILEY. - 2199-160X. ; 6:8
-
Journal article (peer-reviewed)abstract
- This study shows an approach to combine a high electrical conductivity of one composite layer with a high Seebeck coefficient of another composite layer in a double-layer composite, resulting in high thermoelectric power factor. Flexible double-layer-composites, made from Bi2Te3-based-alloy/polylactic acid (BTBA/PLA) composites and Ag/PLA composites, are synthesized by solution additive manufacturing. With the increase in Ag volume-ratio from 26.3% to 41.7% in Ag/PLA layers, the conductivity of the double-layer composites increases from 12 S cm(-1)to 1170 S cm(-1), while the Seebeck coefficient remains approximate to 80 mu V K(-1)at 300 K. With further increase in volume ratio of Ag until 45.6% in Ag/PLA composite layer, the electrical conductivity of the double-layer composites increases to 1710 S cm(-1), however, with a slight decrease of the Seebeck coefficient to 64 mu V K-1. The electrical conductivity and Seebeck coefficient vary only to a limited extent with the temperature. The high Seebeck coefficient is due to scattering of low energy charge carriers across compositionally graded interfaces. A power factor of 875 mu W m(-1) K(-2)is achieved at 360 K for 41.7 vol.% Ag in the Ag/PLA layers. Solution additive manufacturing can directly print this double-layer composite into intricate geometries, making this process is promising for large-scale fabrication of thermoelectric composites.
|
|
| 3. |
- Guo, Sisi, et al.
(author)
-
Thermoelectric Characteristics of Self-Supporting WSe2-Nanosheet/PEDOT-Nanowire Composite Films
- 2023
-
In: ACS Applied Materials and Interfaces. - : AMER CHEMICAL SOC. - 1944-8244 .- 1944-8252. ; 15:29, s. 35430-35438
-
Journal article (peer-reviewed)abstract
- Conducting polymer poly(3,4-ethylenedioxythiophene) nanowires(PEDOTNWs) were synthesized by a modified self-assembled micellar soft-templatemethod, followed by fabrication by vacuum filtration of self-supportingexfoliated WSe2-nanosheet (NS)/PEDOT-NW composite films.The results showed that as the mass fractions of WSe2 NSsincreased from 0 to 20 wt % in the composite films, the electricalconductivity of the samples decreased from & SIM;1700 to & SIM;400S cm(-1), and the Seebeck coefficient increased from12.3 to 23.1 & mu;V K-1 at 300 K. A room-temperaturepower factor of 44.5 & mu;W m(-1) K-2 was achieved at 300 K for the sample containing 5 wt % WSe2 NSs, and a power factor of 67.3 & mu;W m(-1) K-2 was obtained at 380 K. The composite film containing5 wt % WSe2 NSs was mechanically flexible, as shown byits resistance change ratio of 7.1% after bending for 500 cycles ata bending radius of 4 mm. A flexible thermoelectric (TE) power generatorcontaining four TE legs could generate an output power of 52.1 nWat a temperature difference of 28.5 K, corresponding to a power densityof & SIM;0.33 W/m(2). This work demonstrates that the fabricationof inorganic nanosheet/organic nanowire TE composites is an approachto improve the TE properties of conducting polymers.
|
|