1.
  • Anti, Marta-Lena, et al. (author)
  • Effect of silicon on creep properties of titanium 6Al-2Sn-4Zr-2Mo alloy
  • 2020
  • In: MATEC Web of Conferences. - : EDP Sciences. - 2261-236X. ; 321
  • Journal article (peer-reviewed)abstract
    • The alloy Ti-6Al-2Sn-4Zr-2Mo is a titanium alloy for elevated temperatures often used in aerospace applications. Minor additions of silicon have proven to improve the creep resistance of this alloy. In this work, three different amounts of silicon (0.015, 0.07 and 0.162 wt% Si) were added to cast Ti-6242 and creep tests were performed at different temperatures and loads. Creep resistance increased significantly with silicon addition by means of silicide precipitation hindering dislocations movement. Silicon rich nanoparticles in the microstructure were detected and their effect on creep resistance was investigated. The instruments used in this study were light optical microscope (LOM) and scanning electron microscopy (SEM).
  •  
2.
  •  
3.
  • De Mouzon, J, et al. (author)
  • ICMART world report 2011
  • 2015
  • In: HUMAN REPRODUCTION. - 0268-1161. ; 30, s. 59-59
  • Conference paper (other academic/artistic)
  •  
4.
  • Dyer, SJ, et al. (author)
  • ICMART in Africa
  • 2016
  • In: HUMAN REPRODUCTION. - 0268-1161. ; 31, s. 60-60
  • Conference paper (other academic/artistic)
  •  
5.
  •  
6.
  • Engström, Andreas, et al. (author)
  • Synthesis of a TiCN – SiC polyhedron and elongated crystals nanopowder at low nitrogen concentration
  • 2012
  • In: Materials letters (General ed.). - : Elsevier BV. - 0167-577X .- 1873-4979. ; 81, s. 148-150
  • Journal article (peer-reviewed)abstract
    • At room temperature diluted TiCl4 and CCl4 were reduced by sodium particles and mixed with a polycarbomethylsilane (PCS) solution to yield a precursor. It was dried and subsequently annealed at 1300 °C, 1400 °C and 1450 °C in a tube furnace using argon with 10 ppm N2. After the 1450 °C annealing a nanocrystalline powder of TiC0.5 N0.5–SiC polyhedron and elongated crystals was obtained. At the low nitrogen concentration during annealing a gradual nitration is proposed. It is promoted by carbon gaseous species, precursor oxidation, a sufficient temperature and a summarised nitrogen surplus compared to the titanium and carbon amount.
  •  
7.
  •  
8.
  •  
9.
  •  
10.
  •  
Skapa referenser, mejla, bekava och länka
  • Result 1-10 of 10

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Close

Copy and save the link in order to return to this view