1. |
- Korobov, Mikhail V., et al.
(author)
-
Sorption of polar organic solvents and water by graphite oxide : thermodynamic approach
- 2016
-
In: Carbon. - : Elsevier. - 0008-6223 .- 1873-3891. ; 102, s. 297-303
-
Journal article (peer-reviewed)abstract
- Sorption of polar organic solvents CH3OH, C4H8O (THF), CH3CN, C3H7NO (DMF), C2H6OS (DMSO), C5H9NO (NMP) and water was quantitatively evaluated for Hummers (H-GO) and Brodie (B-GO) graphite oxides at T = 298K and at melting temperature (Tm) of the solvents. H-GO showed stronger sorption compared to B-GO for all studied solvents and the increase of sorption upon lowering temperature was observed for both H-GO and B-GO. Thermodynamic equations allowed to explain earlier reported "maximums" of swelling/sorption in the binary systems H-GO – solvent at Tm. The specific relation between the values of enthalpies of sorption and melting leads to the change of sign in enthalpies of sorption at Tm and causes maximal swelling/sorption. The same thermodynamic explanation was given for the "maximum" on the swelling vs. pressure dependence in B-GO and H-GO – H2O systems earlier reported at pressure of phase transition "liquid water-ice VI". Notably higher sorption of H2O was observed for H-GO compared to H-GO membrane (H-GOm) at high relative humidity (RH), RH > 0.75. Experimental sorption isotherm of H-GOm was used to simulate permeation rates of water through H-GOm and to estimate effective diffusion coefficient of water through the membrane.
|
|
2. |
- Rebrikova, Anastasiya T., et al.
(author)
-
Swollen Structures of Brodie Graphite Oxide as Solid Solvates
- 2020
-
In: Journal of Physical Chemistry C. - : American Chemical Society (ACS). - 1932-7447 .- 1932-7455. ; 124:42, s. 23410-23418
-
Journal article (peer-reviewed)abstract
- Swelling of Brodie graphite oxide (B-GO) was studied for a series of normal alcohols from methanol to 1-nonanol. Isopiestic, X-ray diffraction (XRD), thermogravimetric, and differential scanning calorimetry data demonstrated that sorption of polar liquids into GO lamellas formed the set of regular swollen structures, simple binary "solid solvates", characterized by the distance between the GO planes and the value of sorption. Temperature-composition behavior of the swollen structures was adequately described by conventional binary phase diagrams. Phase transformation of the low-temperature swollen structure of B-GO with 1-nonanol gave a clear example of incongruent melting transition typical for the binary solvates. A discreet set of the interplane distances observed by XRD and the stepwise equilibrium desorption pointed to the layered arrangement of solvent molecules in the swollen structures. The swollen structures with one to five parallel layers were observed for a series of normal alcohols with B-GO. The average volume of one layer, 0.36 +/- 0.06 cm(3) g(-1) B-GO, was almost the same for rather different organic liquids and was possibly restricted by the internal geometry of B-GO. This internal volume available for the sorption of the first layer was reasonably estimated from geometrical parameters of B-GO.
|
|
3. |
- Talyzin, Alexandr, et al.
(author)
-
Delamination of graphite oxide in a liquid upon cooling
- 2015
-
In: Nanoscale. - : Royal Society of Chemistry (RSC). - 2040-3364 .- 2040-3372. ; 7:29, s. 12625-12630
-
Journal article (peer-reviewed)abstract
- Graphite oxide (GO) in liquid acetonitrile undergoes a transition from an ordered phase around ambient temperature to a gel-like disordered phase at temperatures below 260 K, as demonstrated by in situ X-ray diffraction. The stacking order of GO layers is restored below the freezing point of acetonitrile (199 K). The reversible swelling transition between a stacked crystalline phase and an amorphous delaminated state observed upon cooling provides an unusual example of increased structural disorder at lower temperatures. The formation of the gel-like phase is attributed to the thermo-responsive conformational change of individual GO flakes induced by stronger solvation. Scanning force microscopy demonstrates that GO flakes deposited onto a solid substrate from acetonitrile dispersions at a temperature below 260 K exhibit corrugations and wrinkling which are not observed for the flakes deposited at ambient temperature. The thermo-responsive transition between the delaminated and stacked phases reported here can be used for sonication-free dispersion of graphene oxide, micro-container applications, or the preparation of new composite materials.
|
|