1.
  • Melk, Latifa, et al. (author)
  • Surface microstructural changes of Spark Plasma Sintered Zirconia after grinding and annealing
  • 2016
  • In: Ceramics International. - : Elsevier BV. - 0272-8842 .- 1873-3956. ; 42:14, s. 15610-15617
  • Journal article (peer-reviewed)abstract
    • Spark plasma sintered zirconia (3Y-TZP) specimens have been produced of 140 nm 372 nm and 753 nm grain sizes by sintering at 1250 C, 1450 C and 1600 C, respectively. The sintered zirconia specimens were grinded using a diamond grinding disc with an average diamond particle size of about 60 µm, under a pressure of 0.9 MPa. The influence of grinding and annealing on the grain size has been analysed. It was shown that thermal etching after of ruff grinding of specimens at 1100 C for one hour induced an irregular surface layer of about a few hundred nanometres in thickness of recrystallized nano-grains, independently of the initial grain size. However, if the ground specimens were exposed to higher temperature, e.g. annealing at 1575 °C for one hour, the nano-grain layer was not observed and the final grain size was similar to that achieved by the same heat treatments on carefully polished specimens. Therefore, by appropriate grinding and thermal etching treatments, nanograined surface layer can be obtained which increases the resistance to low temperature degradation.
  •  
2.
  • Melk, Latifa, et al. (author)
  • The influence of unshielded small cracks in the fracture toughness of yttria and of ceria stabilised zirconia
  • 2016
  • In: Journal of the European Ceramic Society. - : Elsevier BV. - 0955-2219 .- 1873-619X. ; 36:1, s. 147-153
  • Journal article (peer-reviewed)abstract
    • The fracture toughness, KIC of two 3Y–ZrO2 with different grain size (177 and 330 nm) and 12Ce–ZrO2 were determined from a sharp micro-machined notch by Ultra-Short Pulsed Laser Ablation (UPLA) where a micro-cracked zone and non-transformed is generated in front of the notch. The notch plus the damage behaved as an unshielded edge surface crack. The fracture stress, σf of both 330 nm-3Y–ZrO2 and 12Ce–ZrO2 with similar short crack sizes were found to be comparable in despite of their different published R-curves. The results of KIC were discussed in terms of the type of cracks induced and by using a simple R-curve model. It was concluded that for the development of high strength composites with 12Ce–ZrO2 as the matrix, the relevant KIC that controls the σf with surface unshielded short cracks is much closer to the intrinsic KIC than to the indentation KIC or to the plateau KIC of long cracks.
  •  
Skapa referenser, mejla, bekava och länka
  • Result 1-2 of 2
Type of publication
journal article (2)
Type of content
peer-reviewed (2)
Author/Editor
Antti, Marta-Lena (2)
Melk, Latifa (2)
Anglada, Marc (2)
Turon-Vinas, Miquel (2)
Mouzon, Johanne (1)
Akhtar, Farid (1)
show more...
Roa, Joan Josep (1)
show less...
University
Luleå University of Technology (2)
Language
English (2)
Research subject (UKÄ/SCB)
Engineering and Technology (2)
Year
2016 (2)

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Close

Copy and save the link in order to return to this view