1. |
- Aydin, Gökçe, et al.
(author)
-
Influence of laser metal deposition process parameters on a precipitation hardening stainless steel
- 2023
-
In: Welding in the World. - : Springer. - 0043-2288 .- 1878-6669. ; 67:4, s. 1067-1080
-
Journal article (peer-reviewed)abstract
- The combination of corrosion resistance and mechanical properties of martensitic precipitation hardening stainless steels (MPHSS) makes them well suited for demanding applications in aerospace, high-pressure gas bottles, or in injection molding of corrosive plastics. Directed energy deposition methods and specifically the laser metal deposition process with powder as feedstock (LMDp) have the potential to be applied in the production of such components. It is well-known that the geometrical features of the deposited beads such as aspect ratio and dilution are crucial for process efficiency and deposition quality. Therefore, this work aims at understanding the influence of the process parameters and the resulting microstructure of a MPHSS modified PH 13-8Mo alloy when using LMDp. Design of experiment (DoE) was used to plan and analyze the influence and interaction of the different LMDp process variables in the geometry of the deposits. It was found that height, width, and depth were statistically significantly influenced by speed, while height was also considerably influenced by the powder feeding rate. In terms of laser power, it was the most significant factor for the width and the depth, but it did not significantly affect the height of the beads. The results showed that the as-deposited microstructure of the modified PH 13-8Mo under the LMDp conditions investigated in this work consists of a martensitic matrix with some amount of primary δ ferrite. The presence of a low amount of retained austenite and aluminum-enriched inclusions was confirmed. This work enhances the fundamental process and material understanding of LMDp of the modified PH 13-8Mo alloy as a first stage in the fabrication of additively manufactured components.
|
|
2. |
- Aydin, Gökçe, et al.
(author)
-
Towards Laser Metal Deposition of Modified PH 13-8Mo Powder
- 2023
-
In: Key Engineering Materials. - 1013-9826 .- 1662-9795. ; 964, s. 85-90
-
Journal article (peer-reviewed)abstract
- Modified PH 13-8Mo alloy exhibits a good combination of corrosion resistance and mechanical properties for demanding applications in aerospace, petrochemical, and tooling industries. Additive manufacturing, specifically the laser metal deposition process with powder as feedstock (LMDp), has the potential to be utilized in these industries. However, very limited knowledge on the LMDp of this alloy currently exists. The aim of this work was, therefore, to deposit a multi-track single layer of modified PH 13-8Mo alloy as a first step towards 3D geometries, and to analyze the resulting microstructure by using Optical Microscopy, Scanning Electron Microscopy, X-Ray Diffraction, Electron Backscatter Diffraction, and micro-hardness. It was found that the multitrack single layer was free from major defects. The microstructure was heterogeneous, and it consisted of a martensitic matrix and small amounts of δ ferrite, austenite, and AlN. The results of this research will be used to tailor the microstructure and properties of future 3D additively manufactured components.
|
|
3. |
- Baghdadchi, Amir, 1994-, et al.
(author)
-
Corrosion resistance and microstructure analysis of additively manufactured 22% chromium duplex stainless steel by laser metal deposition with wire
- 2023
-
In: Journal of Materials Research and Technology. - 2238-7854 .- 2214-0697. ; 26, s. 6741-6756
-
Journal article (peer-reviewed)abstract
- Microstructure characteristics and pitting corrosion of a duplex stainless steel (DSS) manufactured by laser metal deposition with wire (LMDw) were studied. The layer-by-layer LMDw process resulted in a mixed microstructure of predominantly ferrite with 2% austenite and chromium-rich nitrides, and reheated regions with ~33% austenite. The high cooling rate of LMDw restricted the distribution of Cr, Mo, and Ni, in ferrite and austenite, while N diffuses from ferrite to austenite. Subsequent heat treatment at 1100 C for 1 h resulted in homogenized microstructure, dissolution of nitrides, and balanced ferrite/austenite ratio. It also led to the redistribution of Cr and Mo to ferrite, and Ni and N to austenite. At room temperature, cyclic potentiodynamic polarization measurements in 1.0 M NaCl solution showed no significant differences in corrosion resistance between the as-deposited and heat-treated samples, despite the differences in terms of ferrite to austenite ratio and elemental distribution. Critical pitting temperature (CPT) was the lowest (60 C) for the predominantly ferritic microstructure with finely dispersed chromium-rich nitrides; while reheated area with ~33% austenite in as-deposited condition achieved higher critical temperature comparable to what was obtained after heat treatment (73 and 68 C, respectively). At temperatures above the CPT, selective dissolution of the ferrite after deposition was observed due to depletion of N, while after heat treatment, austenite preferentially dissolved due to Cr and Mo concentrating in ferrite. In summary, results demonstrate how microstructural differences in terms of ferrite-to-austenite ratio, distribution of corrosion-resistant elements, and presence of nitrides affect corrosion resistance of LMDw DSS.
|
|
4. |
- Baghdadchi, Amir, 1994-, et al.
(author)
-
Wire laser metal deposition additive manufacturing of duplex stainless steel components -Development of a systematic methodology
- 2021
-
In: Materials. - : MDPI. - 1996-1944. ; 14:23
-
Journal article (peer-reviewed)abstract
- A systematic four-stage methodology was developed and applied to the Laser Metal Deposition with Wire (LMDw) of a duplex stainless steel (DSS) cylinder > 20 kg. In the four stages, single-bead passes, a single-bead wall, a block, and finally a cylinder were produced. This stepwise approach allowed the development of LMDw process parameters and control systems while the volume of deposited material and the geometrical complexity of components increased. The as-deposited microstructure was inhomogeneous and repetitive, consisting of highly ferritic regions with nitrides and regions with high fractions of austenite. However, there were no cracks or lack of fusion defects; there were only some small pores, and strength and toughness were comparable to those of the corresponding steel grade. A heat treatment for 1 h at 1100 degrees (C) was performed to homogenize the microstructure, remove nitrides, and balance the ferrite and austenite fractions compensating for nitrogen loss occurring during LMDw. The heat treatment increased toughness and ductility and decreased strength, but these still matched steel properties. It was concluded that implementing a systematic methodology with a stepwise increase in the deposited volume and geometrical complexity is a cost-effective way of developing additive manufacturing procedures for the production of significantly sized metallic components.
|
|
5. |
- Baghdadchi, Amir, 1994-, et al.
(author)
-
Wire laser metal deposition of 22% Cr duplex stainless steel : as-deposited and heat-treated microstructure and mechanical properties
- 2022
-
In: Journal of Materials Science. - : Springer Science and Business Media LLC. - 0022-2461 .- 1573-4803. ; 57:21, s. 9556-9575
-
Journal article (peer-reviewed)abstract
- Duplex stainless steel (DSS) blocks with dimensions of 150 × 70x30 mm3 were fabricated by Laser Metal Deposition with Wire (LMDw). Implementation of a programmable logic control system and the hot-wire technology provided a stable and consistent process producing high-quality and virtually defect-free deposits. Microstructure and mechanical properties were studied for as-deposited (AD) material and when heat-treated (HT) for 1 h at 1100 °C. The AD microstructure was inhomogeneous with highly ferritic areas with nitrides and austenitic regions with fine secondary austenite occurring in a periodic manner. Heat treatment produced a homogenized microstructure, free from nitrides and fine secondary austenite, with balanced ferrite and austenite fractions. Although some nitrogen was lost during LMDw, heat treatment or reheating by subsequent passes in AD allowed the formation of about 50% austenite. Mechanical properties fulfilled common requirements on strength and toughness in both as-deposited and heat-treated conditions achieving the highest strength in AD condition and best toughness and ductility in HT condition. Epitaxial ferrite growth, giving elongated grains along the build direction, resulted in somewhat higher toughness in both AD and HT conditions when cracks propagated perpendicular to the build direction. It was concluded that high-quality components can be produced by LMDw and that deposits can be used in either AD or HT conditions. The findings of this research provide valuable input for the fabrication of high-performance DSS AM components
|
|
6. |
- Hosseini, Vahid A., 1987-, et al.
(author)
-
Influence of multiple thermal cycles on microstructure of heat-affected zone in TIG-welded super duplex stainless steel
- 2016
-
In: Welding in the World. - : Springer Verlag. - 0043-2288 .- 1878-6669. ; 60:2, s. 233-245
-
Journal article (peer-reviewed)abstract
- The influence of heat input and multiple welding cycles on the microstructure of the heat-affected zone in autogenously TIG-welded 6 mm 2507 type super duplex stainless steel plates was investigated. In order to produce multiple thermal cycles, one to four pass bead-on-plate welds were made with arc energies of 0.47 and 1.08 kJ/mm, corresponding to heat inputs of 0.37 and 0.87 kJ/mm. Several thermocouples were attached to record thermal cycles on the front and back sides of the plates. Finite element modelling was successfully done to map and correlate measured and calculated peak temperatures. Only minor changes were seen in the ferrite content at 1 and 2 mm from the fusion boundary. Nitrides formed in all passes of the low heat input samples in a region next to the fusion boundary, but only after the third and fourth passes of the high heat input samples. Sigma phase precipitated only in a zone heated to a peak temperature in the range of approximately 828 to 1028 °C. Multiple reheating was found to promote precipitation of sigma phase relatively more than slower cooling. A precipitation free zone was observed between the nitride and sigma phase bands. The precipitation behaviour could be understood from equilibrium phase diagrams, evaluation of local thermal cycles and by correlating results from the modelling and measurements of peak temperatures. It is suggested that the peak temperature, the accumulated time in the critical temperature range between approximately 828 and 1028 °C, and the number of thermal cycles are the most relevant criteria when evaluating the risk of sigma phase formation.
|
|
7. |
- Hosseini, Vahid, 1987-, et al.
(author)
-
Wire-arc additive manufacturing of a duplex stainless steel : thermal cycle analysis and microstructure characterization
- 2019
-
In: Welding in the World. - : Springer Science and Business Media LLC. - 0043-2288 .- 1878-6669. ; 63:4, s. 975-987
-
Journal article (peer-reviewed)abstract
- The evolution of microstructures with thermal cycles was studied for wire-arc additive manufacturing of duplex stainless steel blocks. To produce samples, arc energy of 0.5kJ/mm and interlayer temperature of 150 degrees C were used as low heat input-low interlayer temperature (LHLT) and arc energy of 0.8kJ/mm and interlayer temperature of 250 degrees C as high heat input-high interlayer temperature (HHHT). Thermal cycles were recorded with different thermocouples attached to the substrate as well as the built layers. The microstructure was analyzed using optical and scanning electron microscopy. The results showed that a similar geometry was produced with 14 layers4 beads in each layerfor LHLT and 15 layers3 beads in each layerfor HHHT. Although the number of reheating cycles was higher for LHLT, each layer was reheated for a shorter time at temperatures above 600 degrees C, compared with HHHT. A higher austenite fraction (+8%) was achieved for as-deposited LHLT beads, which experienced faster cooling between 1200 and 800 degrees C. The austenite fraction of the bulk of additively manufactured samples, reheated several times, was quite similar for LHLT and HHHT samples. A higher fraction of secondary phases was found in the HHHT sample due to longer reheating at a high temperature. In conclusion, an acceptable austenite fraction with a low fraction of secondary phases was obtained in the bulk of wire-arc additively manufactured duplex stainless steel samples (35-60%), where higher austenite fractions formed with a larger number of reheating cycles as well as longer reheating at high peak temperatures (800-1200 degrees C).
|
|
8. |
|
|
9. |
- Kisielewicz, Agnieszka, et al.
(author)
-
Hot-Wire Laser-Directed Energy Deposition : Process Characteristics and Benefits of Resistive Pre-Heating of the Feedstock Wire
- 2021
-
In: Metals. - : MDPI. - 2075-4701. ; 11:4, s. 1-25
-
Journal article (peer-reviewed)abstract
- This study investigates the influence of resistive pre-heating of the feedstock wire (here called hot-wire) on the stability of laser-directed energy deposition of Duplex stainless steel. Data acquired online during depositions as well as metallographic investigations revealed the process characteristic and its stability window. The online data, such as electrical signals in the pre-heating circuit and images captured from side-view of the process interaction zone gave insight on the metal transfer between the molten wire and the melt pool. The results show that the characteristics of the process, like laser-wire and wire-melt pool interaction, vary depending on the level of the wire pre-heating. In addition, application of two independent energy sources, laser beam and electrical power, allows fine-tuning of the heat input and increases penetration depth, with little influence on the height and width of the beads. This allows for better process stability as well as elimination of lack of fusion defects. Electrical signals measured in the hot-wire circuit indicate the process stability such that the resistive pre-heating can be used for in-process monitoring. The conclusion is that the resistive pre-heating gives additional means for controlling the stability and the heat input of the laser-directed energy deposition.
|
|
10. |
- Sjölie, Daniel, 1977-, et al.
(author)
-
Integration of Research on Immersive Learning Environments and Education in Welding
- 2024
-
In: Sustainable Production through Advanced Manufacturing, Intelligent Automation and Work Integrated Learning. - : IOS Press. - 9781643685106 - 9781643685113 ; , s. 660-671
-
Book chapter (peer-reviewed)abstract
- The integration of virtual reality (VR) laboratories into welding education presents an array of potential advantages. It can be used at campus or in distance, and it offers an alternative when access to traditional laboratories is challenging. The economic benefits, including savings on material preparation and energy costs, along with the environmental, health and safety advantages of mitigating exposure to welding fumes, arc radiation, and electrical hazards, add further value and contribute to sustainability in welding education. The work presented here is an example of the integration of education in the areas of welding and informatics and research on immersive learning. A multidisciplinary team worked on the development of an immersive learning environment, including virtual laboratory areas for welding processes as well as for microstructural inspection of welds.During the project, this learning environment, and the contained virtual laboratories, have been implemented by the researchers with the support from IT students, and tested, and improved with the feedback provided by students in welding technology, materials science, and manufacturing courses. Overall, more than twenty students from Informatics have been involved throughout the project, resulting in five bachelor theses, three master theses, three course projects in Immersive computing, and two course projects focusing on web development. The involvement of IT students has not only supported the development of the virtual learning environment, but it has also created new avenues for future research and developments in immersive computing.
|
|