1. |
- Cozzolino, Carlo A., et al.
(author)
-
Dye release behavior from polyvinyl alcohol films in a hydro-alcoholic medium : Influence of physicochemical heterogeneity
- 2012
-
In: Colloids and Surfaces A. - : Elsevier BV. - 0927-7757 .- 1873-4359. ; 403, s. 45-53
-
Journal article (peer-reviewed)abstract
- In this paper we investigated the release kinetics of a model drug-like compound (Coomassie brilliant blue) from polyvinyl alcohol (PVOH) films into a hydro-alcoholic solution as a function of the physicochemical properties of the polymer matrix. After 33 days of monitoring, the total amount released ranged from 10% for the high hydrolysis degree/low molecular weight PVOH films to 60% for the low hydrolysis degree/low molecular weight films. Mathematical modeling allowed for an estimation of the two diffusion coefficients (D 1 and D 2) that characterized the release profile of the dye from the films. The degree of hydrolysis dramatically affected both the morphology and the physical structure of the polymer network. A high hydroxyl group content was also associated with the shifting of second order and first order transitions toward higher temperatures, with a concurrent increase in crystallinity. Moreover, the higher the degree of hydrolysis, the higher the affinity of the polymer to the negatively charged molecule dye. Selection of the polymer matrix based on physicochemical criteria may help in achieving different release patterns, thereby representing the first step for the production of polymer systems with modulated release properties.
|
|
2. |
- Cozzolino, Carlo A., et al.
(author)
-
Microfibrillated cellulose and borax as mechanical, O-2-barrier, and surface-modulating agents of pullulan biocomposite coatings on BOPP
- 2016
-
In: Carbohydrate Polymers. - : Elsevier. - 0144-8617 .- 1879-1344. ; 143, s. 179-187
-
Journal article (peer-reviewed)abstract
- Multifunctional composite coatings on bi-oriented polypropylene (BOPP) films were obtained using borax and microfibrillated cellulose (MFC) added to the main pullulan coating polymer. Spectroscopy analyses suggested that a first type of interaction occurred via hydrogen bonding between the C-6-OH group of pullulan and the hydroxyl groups of boric acid, while monodiol and didiol complexation represented a second mechanism. The deposition of the coatings yielded an increase in the elastic modulus of the entire plastic substrate (from similar to 2 GPa of the neat BOPP to similar to 3.1 GPa of the P/B+/MFC-coated BOPP). The addition of MFC yielded a decrease of both static and kinetic coefficients of friction of approximately 22% and 25%, respectively, as compared to the neat BOPP. All composite coatings dramatically increased the oxygen barrier performance of BOPP, especially under dry conditions. The deposition of the high hydrophilic coatings allowed to obtain highly wettable surfaces (water contact angle of similar to 18 degrees).
|
|