| 1. |
- Jarfors, Anders E. W., et al.
(author)
-
Tool wear and life span variations in cold forming operations and their implications in microforming
- 2017
-
In: Technologies. - : MDPI. - 2227-7080. ; 5:1
-
Research review (peer-reviewed)abstract
- The current paper aims to review tooling life span, failure modes and models in cold microforming processes. As there is nearly no information available on tool-life for microforming the starting point was conventional cold forming. In cold forming common failures are (1) over stressing of the tool; (2) abrasive wear; (3) galling or adhesive wear, and (4) fatigue failure. The large variation in tool life observed in production and how to predict this was reviewed as this is important to the viability of microforming based on that the tooling cost takes a higher portion of the part cost. Anisotropic properties of the tool materials affect tool life span and depend on both the as-received and in-service conditions. It was concluded that preconditioning of the tool surface, and coating are important to control wear and fatigue. Properly managed, the detrimental effects from surface particles can be reduced. Under high stress low-cycle fatigue conditions, fatigue failure form internal microstructures and inclusions are common. To improve abrasive wear resistance larger carbides are commonly the solution which will have a negative impact on tooling life as these tend to be the root cause of fatigue failures. This has significant impact on cold microforming.
|
|
| 2. |
- Kasvayee, Keivan Amiri, 1986-, et al.
(author)
-
Microstructural strain mapping during in-situ cyclic testing of ductile iron
- 2018
-
In: Materials Characterization. - : Elsevier. - 1044-5803 .- 1873-4189. ; 140, s. 333-339
-
Journal article (peer-reviewed)abstract
- This paper focuses on local strain distribution in the microstructure of high silicon ductile iron during cyclic loading. In-situ cyclic test was performed on compact-tension (CT) samples inside the scanning electron microscope (SEM) to record the whole deformation and obtain micrographs for microstructural strain measurement by means of digital image correlation (DIC) technique. Focused ion beam (FIB) milling was used to generate speckle patterns necessary for DIC measurement. The equivalent Von Mises strain distribution was measured in the microstructure at the maximum applied load. The results revealed a heterogeneous strain distribution at the microstructural level with higher strain gradients close to the notch of the CT sample and accumulated strain bands between graphite particles. Local strain ahead of the early initiated micro-cracks was quantitatively measured, showing high strain localization, which decreased by moving away from the micro-crack tip. It could be observed that the peak of strain in the field of view was not necessarily located ahead of the micro-cracks tip which could be because of the (i) strain relaxation due to the presence of other micro-cracks and/or (ii) presence of subsurface microstructural features such as graphite particles that influenced the strain concentration on the surface.
|
|