1. |
- Chen, Haiwei, et al.
(author)
-
Extending the environmental lifetime of unpackaged perovskite solar cells through interfacial design
- 2016
-
In: Journal of Materials Chemistry A. - : Royal Society of Chemistry (RSC). - 2050-7488 .- 2050-7496. ; 4:30, s. 11604-11610
-
Journal article (peer-reviewed)abstract
- Solution-processed oxo-functionalized graphene (oxo-G1) is employed to substitute hydrophilic PEDOT:PSS as an anode interfacial layer for perovskite solar cells. The resulting devices exhibit a reasonably high power conversion efficiency (PCE) of 15.2% in the planar inverted architecture with oxo-G1 as a hole transporting material (HTM), and most importantly, deploy the full open-circuit voltage (Voc) of up to 1.1 V. Moreover, oxo-G1 effectively slows down the ingress of water vapor into the device stack resulting in significantly enhanced environmental stability of unpackaged cells under illumination with 80% of the initial PCE being reached after 500 h. Without encapsulation, ∼60% of the initial PCE is retained after ∼1000 h of light soaking under 0.5 sun and ambient conditions maintaining the temperature beneath 30 °C. Moreover, the unsealed perovskite device retains 92% of its initial PCE after about 1900 h under ambient conditions and in the dark. Our results underpin that controlling water diffusion into perovskite cells through advanced interface engineering is a crucial step towards prolonged environmental stability.
|
|
2. |
- Luo, Xiyu, et al.
(author)
-
Effects of local compositional heterogeneity in mixed halide perovskites on blue electroluminescence
- 2024
-
In: Matter. - 2590-2393. ; 7:3, s. 1054-1070
-
Journal article (peer-reviewed)abstract
- Compositional heterogeneity is commonly observed in mixed bromide/iodide perovskite photoabsorbers, typically with minimal effects on charge carrier recombination and photovoltaic performance. Consistently, it has so far received very limited attention in bromide/chloride-mixed perovskites, which hold particular significance for blue light-emitting diodes. Here, we uncover that even a minor degree of localized halide heterogeneity leads to severe non-radiative losses in mixed bromide/chloride blue perovskite emitters, presenting a stark contrast to general observations in photovoltaics. We not only provide a visualization of the heterogeneity landscape spanning from micro-to sub-microscale but also identify that this issue mainly arises from the initially formed chloride-rich clusters during perovskite nucleation. Our work sheds light on a long-term neglected factor impeding the advancement of blue light-emitting diodes using mixed halide perovskites and provides a practical strategy to mitigate this issue.
|
|