1. |
- Dahlin, Peter, 1971-
(author)
-
Growth of fatigue cracks subjected to non-proportional Mode I and II
- 2005
-
Doctoral thesis (other academic/artistic)abstract
- This thesis deals with some aspects of crack growth in the presence of cyclic loading, i.e. fatigue. The cyclic load cases studied here are primary of non-proportional mixed mode type. Under non-proportional loading the principal stress directions rotate and, generally, the ratio between the principal stresses vary. A new criterion has been presented for prediction of incipient crack path direction after changes in load from steady Mode I to non-proportional loading.The criterion is based on FE-simulations which are used to compute the actual elasto-plastic stress state in the vicinity of the crack tip. The predictions of the criterion capture several phenomena observed in the literature, which indicates that plasticity effects have to be included in a criterion for crack path predictions under non-proportional loading. The effects of Mode II overloads on subsequent Mode I crack growth have been studied relatively little in the literature. Also, the results deviates substantially. In the present thesis, this load case has been investigated in detail, both experimentally and analytically. The results show that the Mode I crack growth rate decreases after a single Mode II load, if the R-ratio is not as high as to keep the entire Mode I load cycle above the closure level. This is based on the fact, shown in this thesis, that the reduction is caused by crack closure due to tangential displacement of crack-surface irregularities.A new loading device is presented. With this device, it is possible to apply sequential loading in Mode I and Mode II in an automated way, without having to dismount the specimens. This loading device is used to study the influence of periodic Mode II loading on Mode I crack growth. The main parameters concerning the influence of periodic Mode II loading on Mode I crack growth are; (i) the Mode I R-ratio, (ii) the Mode II magnitude and (iii) the Mode II periodicity, M (number of Mode I loads for every Mode II load). The mechanisms involved are mainly RICC (Roughness-Induced Crack Closure) and a Mode II mechanism that increases the growth rate temporary at every Mode II load. Hence, the latter becomes more significant for low M-values. The higher the Mode I R-ratio the smaller is the reduction.
|
|
2. |
|
|
3. |
|
|
4. |
- Barsoum, Imad
(author)
-
Ductile failure and rupture mechanisms in combined tension and shear
- 2006
-
Licentiate thesis (other academic/artistic)abstract
- This licentiate thesis is generally concerned with the ductile failure and rupture mechanisms encountered under combined tension and torsion loading. In the first part entitled Paper A, an experimental investigation of the rupture mechanisms in a mid-strength and a high strength steel was conducted employing a novel test configuration. The specimen used was a double notched tube specimen loaded in combined tension and torsion at a fixed ratio. The effective plastic strain, the stress triaxiality and the Lode parameter was determined in the centre of the notch at failure. Scanning electron microscopy of the fractured surfaces revealed two distinctively different ductile rupture mechanisms depending on the stress state. At high stress triaxiality the fractured surfaces were covered with large and deep dimples, suggesting that growth and internal necking of voids being the governing rupture mechanism. At low triaxiality it was found that the fractured surfaces were covered with elongated small shear dimples, suggesting internal void shearing being the governing rupture mechanism. In the fractured surfaces of the high-strength steel, regions with quasi-cleavage were also observed. The transition from the internal necking mechanism to the internal shearing mechanism was accompanied by a significant drop in ductility.In the second part entitled Paper B, a micromechanics model based on the theoretical framework of plastic localization into a band introduced by Rice is developed. The model employed consists of a planar band with a square array of equally sized cells, with a spherical void located in the centre of each cell. The periodic arrangement of the cells allows the study of a single unit cell for which fully periodic boundary conditions are applied. The micromechanics model is applied to analyze failure by ductile rupture in experiments on double notched tube specimens subjected to combined tension and torsion carried out by the present authors. The stress state is characterized in terms of the stress triaxiality and the Lode parameter. Two rupture mechanisms can be identified, void coalescence by internal necking at high triaxiality and void coalescence by internal shearing at low triaxiality. For the internal necking mechanism, failure is assumed to occur when the deformation localizes into a planar band and is closely associated with extensive void growth. For the internal shearing mechanism, a simple criterion based on the attainment of a critical value of shear deformation is utilized. The two failure criteria capture the transition between the two rupture mechanisms successfully and are in good agreement with the experimental result.
|
|
5. |
- Barsoum, Imad, 1978-
(author)
-
The effect of stress state in ductile failure
- 2008
-
Doctoral thesis (other academic/artistic)abstract
- The industrial application of high strength steels in structural components has increased the demand on understanding the ductile failure behavior of this type of materials. In practical situations the loading experienced on components made out of these materials can be very complex, which may affect the failure behavior.The objective of this work is to study the effect of stress state on ductile failure and the mechanisms leading to rupture in high strength steels. The stress state is characterized by the stress triaxiality T and the Lode parameter L, which is a deviatoric stress state parameter that discriminates between axisymmetric or shear dominated stress states. For this purpose experiments on two different specimen configurations are performed; a double notched tube (DNT) specimen tested in combined tension and shear and a round notched bar (RNB) specimen tested in uniaxial tension. The two specimens give rise to different stress states at failure in terms of T and L. The failure loci for the DNT specimen show an abrupt change in ductility, indicating a transition between the rupture mechanisms necking of intervoid ligaments and shearing of intervoid ligaments. A clear difference in ductility between the two specimen configurations is also observed, which is closely associated with the difference in stress state at failure.A micromechanical model is developed, which assumes that ductile material failure occurs when the deformation becomes highly non-linear and localizes into a band. The model, which is applied to analyze the experiments, consists of a band with a square array of equally sized cells, with a spherical void located in the center of each cell. The model, extended with a shear criterion, captures the experimental trend rather well. The model also shows that the effect of the deviatoric stress state (L) on void growth, void shape evolution and coalescence is significant, especially at low levels of T and shear dominated stress state.
|
|
6. |
|
|
7. |
- Cadario, Alessandro, 1975-
(author)
-
Life prediction and mechanisms for the initiation and growth of short cracks under fretting fatigue loading
- 2006
-
Doctoral thesis (other academic/artistic)abstract
- Fretting fatigue is a damage process that may arise in engineering applications where small cyclic relative displacements develop inside contacts leading to detrimental effects on the material fatigue properties. Fretting is located in regions not easily accessible, which makes it a dangerous phenomenon. It is therefore important to be able to make reliable predictions of the fretting fatigue lives.The work presented in this thesis has its focus on different aspects related to fretting fatigue in the titanium alloy Ti-17. A fretting experiment was developed which allowed for separate control of the three main fretting loads. Initially, the evolution of the coefficient of friction inside the slip region was investigated experimentally and analytically. Subsequently, 28 fretting tests were performed in which large fatigue cracks developed.The fretting tests were firstly evaluated with respect to fatigue crack initiation through five multiaxial fatigue criteria. The criteria predicted a too high fretting fatigue limit. A possible clue to the discrepancy was found in the fretting induced surface roughness with the asperity-pit interactions.The fatigue growth of the large fretting cracks was numerically modelled through a parametric crack growth procedure. The predicted lives were compared to the experimental outcome. The numerical simulations showed that linear elastic fracture mechanics was an appropriate tool for the prediction of fretting fatigue propagation lives in the long crack regime.Fatigue cracks spend most of their propagation life in the small crack regime. The possibility of modelling the small crack behaviour is therefore very important from the engineering point of view. The fatigue growth of through thickness short cracks was studied experimentally and numerically in the four-point bend configuration. It was found that linear elastic fracture mechanics and closure-free material growth data furnished conservative estimates for cracks longer than 50 μm.One method to improve fretting fatigue life is to shot peen the contact surfaces. Experimental results on fretting life with or without shot peening were simulated. The fatigue life enhancement in shot peened specimens could be explained by slower crack growth in the surface material layer with residual compressive stresses.
|
|
8. |
|
|
9. |
|
|
10. |
- Dahlberg, Johan, 1977-
(author)
-
On the asperity point load mechanism for rolling contact fatigue
- 2007
-
Doctoral thesis (other academic/artistic)abstract
- Rolling contact fatigue is a damage process that may arise in mechanical applications with repeated rolling contacts. Some examples are: gears; cams; bearings; rail/wheel contacts. The resulting damage is often visible with the naked eye as millimeter sized surface craters. The surface craters are here denoted spalls and the gear contact served as a case study.The work focused on the asperity point load mechanism for initiation of spalls. It was found that the stresses at asperity level may be large enough to initiate surface cracking, especially if the complete stress cycle was accounted for.The gear contact is often treated as a cylindrical contact. The thesis contains experimental and numerical results connected to rolling contact fatigue of cylindrical contacts. At the outset a stationary cylindrical contact was studied experimentally. The stationary test procedure was used instead of a rolling contact. In this way the number of contact parameters was minimized. The cylindrical contact resulted in four different contact fatigue cracks. The two cracks that appeared first initiated below the contact. The other two cracks developed at the contact surface when the number of load cycles and the contact load increased.The influence of a surface irregularity (asperity) was studied numerically with the Finite Element Method (FEM). Firstly, the stationary contact was modelled and investigated numerically. At the cylindrical contact boundary a single axisymmetric was included. The partially loaded asperity introduced a tensile surface stress, which seen from the asperity centre was radially directed. Secondly, FE simulations were performed where a single axisymmetric asperity was over-rolled by a cylindrical contact. The simulations were performed for pure rolling and rolling with slip. For both situations, tensile forward directed stresses in front of the asperity were found. The presence of slip and a surface traction greatly increased the stresses in front of the asperity. Finally, when rolling started from rest with applied slip, the distance to steady-state rolling was determined for elastic similar cylindrical rollers.
|
|