1. |
- Abadei, Saeed, 1961, et al.
(author)
-
Low frequency characterisation of laser ablation deposited thin Na0.5K0.5NbO3 (NKN) films for microwave application
- 2001
-
In: Integrated Ferroelectrics. - : Informa UK Limited. - 1058-4587 .- 1607-8489. ; 263:1, s. 173-179
-
Journal article (peer-reviewed)abstract
- Experimental results on three types of Na0.5K0.5NbO3 (NKN) film capacitor structures are presented. The epitaxial NKN thin films have been deposited on (100) Si (high resistivity), SiO2/Si (low resistivity) and Pt/Si (low resistivity) substrates using laser ablation deposition. Both straight slot and interdigital electrode have been deposited on top of the NKN films. The leakage current and low frequency dielectric properties (I-V, C-V, tanδ-V) of the structures have been measured at 1 MHz as a function of electric field at room temperature. In all three types of capacitor structures the leakage currents in a-b plane are very small, while along c-axis there are extremely large leakage currents. On low resistivity silicon substrates the tunability of the dielectric permittivity is about 12% and loss tangent is low also. On high resistivity (ρ>10 kOhm cm) silicon substrate the tunability at 1 MHz is extremely high, about 10 times, and the losses are also high. On the other hand at microwave frequencies the losses are small (tanδ
|
|
2. |
- Abadei, S., et al.
(author)
-
Microwave properties of tunable capacitors basee on magnetron sputtered ferroelectric Na0.5K0.5NbO3 film on low and high resistivity silicon substrates
- 2001
-
In: Integrated Ferroelectrics. - : Informa UK Limited. - 1058-4587 .- 1607-8489. ; 39:1-4, s. 359-366
-
Conference paper (other academic/artistic)abstract
- In this work, small signal DC voltage dependent dielectric permittivity, loss tangent, and tuneability of magnetron sputtered epitaxial Na0.5K0.5NO3 films are studied experimentally. (100)-oriented Na0.5K0.5NbO3 films are deposited onto SiO2-buffered CMOS grade low resistivity (p = 10-20 cm) and high resistivity (p = 15-45 kcm) silicon substrates. Planar capacitors with 2 or 4 m gaps between electrodes have been fabricated on top of ferroelectric films. These devices have been characterized in the frequency range 1.0 MHz to 50 GHz at temperatures 30 - 300K. Na0.5K0.5NbO3/SiO2/Si structures on high resistivity silicon substrate exhibit C-V performances typical for Metal-Insulator- Semiconductor (MIS) capacitors. At low frequencies, f 1.0 GHz, the large tuneability and large losses are associated with the MIS structure, while at higher microwave frequencies the tuneability is mainly associated with the ferroelectric, film. At 1.0 MHz and room temperature, the tuneability of Na0.5K0.5NbO3/SiO2/Si structures more than 90%, reducing to 10-15 % at 50 GHz. The losses decrease with increasing the DC bias and frequency. A Q-factor more than 15 at 50 GHz is observed. The dielectric permittivity of the Na0.5K0.5NbO3 film is in the range 50-150 at frequencies 0.045-50 GHz. On low resistivity substrate the performance of Na0.5K0.5NbO3 films is completely screened by the high losses in silicon, and the tuneability is negligible. © 2001 Taylor and Francis.
|
|
3. |
- Blomqvist, Mats, et al.
(author)
-
Electro-optic effect in ferroelectric Na0.5K0.5NbO3 thin films on oxide substrates
- 2006
-
In: Integrated Ferroelectrics. - : Informa UK Limited. - 1058-4587 .- 1607-8489. ; 80:1, s. 97-106
-
Journal article (peer-reviewed)abstract
- We have deposited Na0.5NbO3 (NKN) films oil single crystal Al2O3(1 (1) under bar 02) and SrTiO3(001) substrates using rf-magnetron sputtering of a stoichiometric, high-density ceramic target. Using x-ray diffraction it was confirmed that NKN grows preferentially c-axis oriented on sapphire substrate and epitaxially oil the perovskite SrTiO3(001) substrate. Electro-optical (EO) properties were measured in visible light through a transverse method. With an applied dc field up to 20 kV/cm, the effective linear EO response was determined to r(eff) = 28 pm/V for NKN/Al2O3 and r(eff) = I I pm/V for NKN/SrTiO3, where a superlinear dependence was observed.
|
|
4. |
- Blomqvist, Mats, et al.
(author)
-
Rf sputtered Na0.5K0.5NbO3 films on oxide substrates as optical waveguiding material
- 2003
-
In: Integrated Ferroelectrics. - : Informa UK Limited. - 1058-4587 .- 1607-8489. ; 54, s. 631-640
-
Journal article (peer-reviewed)abstract
- Highly crystalline Na0.5K0.5NbO3 (NKN) thin films of 1-2 mum thickness were deposited by rf-magnetron sputtering of a stoichiometric, ceramic target on single crystal LaAlO3 (001) and Al2O3 (01 (1) under bar2) substrates. X-ray diffraction measurements revealed epitaxial quality of NKN/LaAlO3 film structures, whereas NKN films on sapphire substrates were found to be preferentially c -axis oriented. A prism-coupling technique was used to characterize optical and waveguiding properties. A bright-line spectrum at lambda = 632.8 nm, revealed sharp peaks, corresponding to transverse magnetic (TM) and electric (TE) waveguide propagation modes in NKN/LaAlO3 and NKN/Al2O3 thin films. Using a least mean square fit the refractive index for the films and film thickness were calculated. The extraordinary and ordinary refractive indices were determined to n(e) = 2.207 +/- 0.002 and n(o) = 2.261 +/- 0.002, and n(e) = 2.216 +/- 0.002 and n(o) = 2.247 +/- 0.002 at lambda = 632.8 nm for 2.0 mum thick NKN films on LaAlO3 and Al2O3 , respectively. This corresponds to a birefringence Deltan = n(e) - n(o) = -0.054 +/- 0.003 and Deltan = -0.031 +/- 0.003 in the films, where the larger Deltan for the NKN/LaAlO3 structure can be explained by the superior crystalline quality compared to NKN/Al2O3 . Atomic force microscopy images of the film surfaces revealed rms roughnesses of 2.5 nm and 8.0 nm for 1.0-mum thick NKN/LaAlO3 and NKN/Al2O3 films, respectively. We believe surface scattering is one of the main sources of waveguide losses in the thin films.
|
|
5. |
- Blomqvist, Mats, et al.
(author)
-
Visible and IR light waveguiding in ferroelectric Na0.5K0.5NbO3 thin films
- 2005
-
In: Integrated Ferroelectrics. - : Informa UK Limited. - 1058-4587 .- 1607-8489. ; 69, s. 277-286
-
Journal article (peer-reviewed)abstract
- High-quality ferroelectric thin films are attractive materials for integrated optics applications including electro-optic waveguide modulators and frequency doubling secondharmonic generators. Several fefroelectric thin film materials, such as BaTiO3, KNbO3, LiNbO3, and (Pb,La)(ZrTi)O-3, have been investigated regarding their optical and waveguiding properties. Recently the first results on waveguiding in ferroelectric Na0.5K0.5NbO3 (NKN) thin films were presented. Perovskite NKN films have previously been investigated as electrically tunable material for low loss rf and microwave applications. Na0.5K0.5NbO3 thin films of thickness 0.5-1.0 mum have been deposited on Nd:YAlO3(001) and Al2O3(0112) substrates using rf-magnetron sputtering of a stoichiometric, high-density ceramic target. X-ray diffraction measurements confirmed films grown highly (00l) oriented on the perovskite Nd:YAlO3 substrate and preferentially c-axis oriented on the single crystal r-cut sapphire substrate. Optical and waveguiding properties were characterized using a Metricon 2010 prism-coupling apparatus with a rutile prism. Dark-line spectra were obtained at visible light (lambda = 632.8 nm) as well as at infrared optical communication wavelengths, lambda = 1319 nm and lambda = 1549 nm, in both transverse electric (TE) and transverse magnetic (TM) polarizations. Sharp dips corresponding to waveguide propagation modes in the thin film layers where observed for both substrates. The calculated refractive index values and corresponding birefringence (Deltan = n(TM) - n(TE) = n(e) - n(o)) as a function of wavelength has been compared. Generally a larger birefringence is observed for the NKN film on Nd:YAlO3, which is in agreement with the larger degree of preferential c-axis orientation measured by XRD.
|
|
6. |
- Chen, Kai, et al.
(author)
-
Self-Assembled Core-Shell Polymer Dielectric Prepared by Solution Casting Process
- 2009
-
In: Integrated Ferroelectrics. - : Taylor andamp; Francis: STM, Behavioural Science and Public Health Titles. - 1058-4587 .- 1607-8489. ; 113, s. 1-8
-
Journal article (peer-reviewed)abstract
- Giant permittivity at 1 MHz, which slightly changes with temperatures, is observed in a polymer composite. The dielectric spectroscopy demonstrates that the samples are electrically heterogeneous. The microstructure observation and the ingredient analysis evidence they self assemble the conducting cores surrounded by the insulating shells. The giant-dielectric phenomenon is therefore attributed to the percolation effect. The electrically heterogeneous microstructure with effective permittivity values about 10 000 can be fabricated by a simple solution casting process in air. The composite is an attractive option to the currently used printing dielectric and the future flexible electronics.
|
|
7. |
- Cho, C. R., et al.
(author)
-
Ferroelectric Na0.5K0.5NbO3 thin films by pulsed laser deposition
- 2000
-
In: Integrated Ferroelectrics. - : Informa UK Limited. - 1058-4587 .- 1607-8489. ; 31:1-4, s. 35-45
-
Journal article (peer-reviewed)abstract
- Highly c-axis oriented single phase Na0.5K0.5NbO3 (NKN) thin films have been deposited onto polycrystalline Pt80Ir20 substrates and SiO2/Si(001) wafers using pulsed laser ablation of stoichiometric ceramic target. Strong self-assembling of NKN films along the [001] direction has been observed. Properties of NKN/Pt thin film structures have been successfully tailored by oxygen pressure control from the ferroelectric state, characterized by the remnant polarization of 12 muC/cm(2), dielectric constant epsilon similar to 520 and tan delta - 0.024 @ 100 kHz, to superparaelectric state with tan delta as low as 0.003 and epsilon = 210 with very small 1.7% dispersion in the frequency domain 0.4-100 kHz and less than 10% Variation in the temperature range 77-415 K. NKN films grown onto SiO2/Si(001) substrates show quadrupled super-lattice structure along c-axis, loss tan delta less than 0.01, and epsilon similar to 110 @ 1 MHz. C-V measure ments for Au/NKN(270nm)/SiO2/Si MFIS-diode structure yield memory window of 3.26 V at the programmable voltage of 8 V.
|
|
8. |
- Cho, C. R., et al.
(author)
-
Na0.5K0.5NbO3 thin films for MFIS_FET type non-volatile memory applications
- 2002
-
In: Integrated Ferroelectrics. - 1058-4587 .- 1607-8489. ; 49, s. 21-30
-
Journal article (peer-reviewed)abstract
- Na0.5K0.5NbO3(NKN) thin films have been prepared on Pt80Ir20, SiO2/Si, and Ta2O5/Si substrates for ferroelectric non-volatile memory applications. Ferroelectric hysteresis loops for Au/NKN/Pt80Ir20 vertical capacitor yielded remnant polarization of 12 muC/cm(2) and coercive field similar to20 kV/cm. Significant flat-band voltage V-FB shifts with buffer layer thickness in Au/NKN/SiO2/Si structures have been attributed to the intermixing between Na and K alkali ions and SiO2 layer. On the other hand, Au/NKN/Ta2O5/Si structure exhibited wide memory window without significant V-FB deviations, low leakage currents, and rather long retention time at zero bias.
|
|
9. |
- Cho, C. R., et al.
(author)
-
Thickness dependent performance of Na0.5K0.5NbO3/sapphire thin film varactors
- 2001
-
In: Integrated Ferroelectrics. - 1058-4587 .- 1607-8489. ; 39:1-4, s. 1353-1360
-
Journal article (peer-reviewed)abstract
- Perfect c-axis oriented Na0.5K0.5NbO3 (NKN) films have been pulsed laser deposited on Al2O3(01 (1) under bar2) single crystals (r-cut sapphire) for voltage tunable microwave device applications. Thickness dependence of dielectric performance of the NKN/sapphire interdigital capacitors (IDCs) has been studied. 40 V bias tunability and dielectric loss tandelta of 4 burr slot IDCs have been found to be 24.6 % and 2.86 % for 1.2 mum thick NKN film, and 6.1 % and 0.83 % for 0.14 mum thick NKN film, respectively. Low leakage currents and high breakdown voltages are observed in these structures.
|
|
10. |
- Gevorgian, Spartak, 1948, et al.
(author)
-
ADS Based 1D Model of Solidly Mounted FBARs Including Longitudinal and Shear Waves
- 2012
-
In: Integrated Ferroelectrics. - : Informa UK Limited. - 1058-4587 .- 1607-8489. ; 134:1, s. 75-80
-
Journal article (peer-reviewed)abstract
- ADS based Mason circuit model of solidly mounted FBARs is proposed where coexistence of both thickness mode longitudinal and shearwaves is assumed. While calculating the leakage of longitudinal and shear waves into the substrate via Bragg reflector the model takes into account multiple reflections from top and bottom electrodes. The results of modeling are useful in optimization of ferroelectric film deposition process and the design of the resonators.
|
|