1. |
- Litnovsky, Andrey, et al.
(author)
-
Carbon transport, deposition and fuel accumulation in castellated structures exposed in TEXTOR
- 2007
-
In: Journal of Nuclear Materials. - : Elsevier BV. - 0022-3115 .- 1873-4820. ; 367, s. 1481-1486
-
Journal article (peer-reviewed)abstract
- In order to maintain the thermo-mechanical durability of ITER it is proposed to castellate the interior surface of the first wall and divertor by splitting them into small-size cells [W. Daener et a]., Fusion Eng. Des. 61&62 (2002) 61]. A concern is the accumulation of fuel in the gaps of the castellation. In TEXTOR, molybdenum limiters were exposed in the scrape-off layer (SOL) plasma to assess fuel accumulation. The first limiter was exposed under deposition-dominated conditions. Carbon deposits were formed both on top surfaces and in the gaps. About 0.12% of the impinging D-fluence was found in the gaps. Another castellated limiter was exposed under erosion-dominated conditions. Deposited layers were found only on the plasma shadowed areas of the gaps. A significant amount of molybdenum from the limiter was found intermixed in the deposit. The gaps contained similar to 0.03% of the impinging D-fluence. Modeling was performed to simulate carbon transport into the gaps.
|
|
2. |
- Litnovsky, A., et al.
(author)
-
Carbon deposition and fuel accumulation in a castellated limiter exposed under erosion-dominated conditions in the SOL of TEXTOR
- 2005
-
In: 32nd EPS Conference on Plasma Physics 2005, EPS 2005, Held with the 8th International Workshop on Fast Ignition of Fusion Targets. - 9781622763320 ; , s. 361-364
-
Conference paper (peer-reviewed)abstract
- Castellated limiter with ITER-like geometry was exposed under the erosion-dominated conditions in the SOL of TEXTOR. After the exposure, deposits were found in the gaps, with a negligible amount of deposited material that was detected on top surfaces open to the plasma. The thickest deposits are located on plasma shadowed sides of the gaps with maximum thickness up to 0.5 μm on the plasma closest locations as it was measured with SIMS diagnostic. The deposit thickness decrease exponentially with the depth of gaps with e-folding length of 1.7-2 mm as inferred from EPMA measurements. Material intermixing was found to occur in the deposited layers. Deposits are mixed Mo:C:D:O:B:H layers. Gaps contain at least (5÷10)×1016 of D fuel atoms per cm2. This corresponds roughly to 0.02÷0.04 % of total averaged D fluence impinging on the castellation.
|
|
3. |
- Litnovsky, A., et al.
(author)
-
Diagnostic mirrors for ITER : A material choice and the impact of erosion and deposition on their performance
- 2007
-
In: Journal of Nuclear Materials. - : Elsevier BV. - 0022-3115 .- 1873-4820. ; 363, s. 1395-1402
-
Journal article (peer-reviewed)abstract
- Metal mirrors will be implemented in about half of the ITER diagnostics. Mirrors in ITER will have to withstand radiation loads, erosion by charge-exchange neutrals, deposition of impurities, particle implantation and neutron irradiation. It is believed that the optical properties of diagnostic mirrors will be primarily influenced by erosion and deposition. A solution is needed for optimal performance of mirrors in ITER throughout the entire lifetime of the machine. A multi-machine research on diagnostic mirrors is currently underway in fusion facilities at several institutions and laboratories worldwide. Among others, dedicated investigations of ITER-candidate mirror materials are ongoing in Tore-Supra, TEXTOR, DIII-D, TCV, T-10 and JET. Laboratory studies are underway at IPP Kharkov (Ukraine), Kurchatov Institute (Russia) and the University of Basel (Switzerland). An overview of current research on diagnostic mirrors along with an outlook on future investigations is the subject of this paper.
|
|
4. |
- Litnovsky, A., et al.
(author)
-
Direct comparative test of single crystal and polycrystalline diagnostic mirrors exposed in TEXTOR in erosion conditions
- 2005
-
In: 32nd EPS Conference on Plasma Physics 2005, EPS 2005, Held with the 8th International Workshop on Fast Ignition of Fusion Targets. - 9781622763320 ; , s. 1726-1729
-
Conference paper (peer-reviewed)abstract
- First direct comparative test of single crystal and polycrystalline diagnostic mirror materials under erosion conditions has been made in TEXTOR. Before exposure in TEXTOR, glow discharge cleaning has efficiently restored the reflectivity of initially oxidized mirrors. After the exposure, no significant changes in total reflectivity were observed. Drastic increase of diffuse reflectivity was measured for polycrystalline molybdenum mirror, but not for the single crystal. Thus, specular reflectivity of single crystal is significantly higher than of polycrystalline one. The most affected wavelength range is 250-1000 nm, no significant changes of reflectivity was noticed in the range 1000-2000 nm. No or negligible effect of erosion on polarization characteristics of mirrors was measured.
|
|
5. |
- Sergienko, G., et al.
(author)
-
Erosion of a tungsten limiter under high heat flux in TEXTOR
- 2007
-
In: Journal of Nuclear Materials. - : Elsevier BV. - 0022-3115 .- 1873-4820. ; 363, s. 96-100
-
Journal article (peer-reviewed)abstract
- Erosion characteristics of a tungsten plate heated up in TEXTOR by the plasma load have been investigated at temperatures extending to the melting point. No enhancement of atomic release exceeding physical sputtering and normal thermal sublimation for temperatures below 3700 K was observed. The liquid tungsten moved fast along the plate in the direction perpendicular to the magnetic field lines. The motion is caused by the Lorentz force due to the thermoelectron current emitted from the hot tungsten surface. The motion of liquid tungsten caused a material loss of 2.85 g during two discharges. The material redistribution due to the melt layer motion is compared with a MEMOS-1.5D simulation.
|
|
6. |
- Sergienko, G., et al.
(author)
-
Experience with bulk tungsten test-limiters under high heat loads : melting and melt layer propagation
- 2007
-
In: Physica Scripta. - 0031-8949 .- 1402-4896. ; T128, s. 81-86
-
Journal article (peer-reviewed)abstract
- The paper provides an overview of processes and underlying physics governing tungsten melt erosion in the fusion plasma environment. Experiments with three different bulk tungsten test-limiters were performed in TEXTOR: (i) thermally insulated solid plate fixed on a graphite roof-like limiter heated up by the plasma to the melting point, (ii) macro-brush of the ITER-relevant castellated structure and (iii) lamellae structure developed for the JET divertor. The main objectives were to determine the metal surface damage, the formation of the melt layer and its motion in the magnetic field. PHEMOBRID-3D and MEMOS-1.5D numerical codes were used to simulate the experiment with the roof-like test-limiter. Both experiments and simulation showed that the melting of tungsten can lead to a large material redistribution due to thermo-electron emission currents without ejection of molten material to the plasma.
|
|