1. |
- Ding, Yang, et al.
(författare)
-
Structural phase transition of vanadium at 69 GPa
- 2007
-
Ingår i: Physical Review Letters. - 0031-9007 .- 1079-7114. ; 98:8
-
Tidskriftsartikel (refereegranskat)abstract
- A phase transition was observed at 63-69 GPa and room temperature in vanadium with synchrotron x-ray diffraction. The transition is characterized as a rhombohedral lattice distortion of the body-centered-cubic vanadium without a discontinuity in the pressure-volume data, thus representing a novel type of transition that has never been observed in elements. Instead of driven by the conventional s-d electronic transition mechanism, the phase transition could be associated with the softening of C-44 trigonal elasticity tensor that originates from the combination of Fermi surface nesting, band Jahn-Teller distortion, and electronic topological transition.
|
|
2. |
- Zeng, Qiao-Shi, et al.
(författare)
-
Substitutional alloy of Ce and Al
- 2009
-
Ingår i: Proceedings of the National Academy of Sciences of the United States of America. - : Proceedings of the National Academy of Sciences. - 0027-8424 .- 1091-6490. ; 106:8, s. 2515-2518
-
Tidskriftsartikel (refereegranskat)abstract
- The formation of substitutional alloys has been restricted to elements with similar atomic radii and electronegativity. Using high-pressure at 298 K, we synthesized a face-centered cubic disordered alloy of highly dissimilar elements (large Ce and small Al atoms) by compressing the Ce3Al intermetallic compound > 15 GPa or the Ce3Al metallic glass > 25 GPa. Synchrotron X-ray diffraction, Ce L-3-edge absorption spectroscopy, and ab initio calculations revealed that the pressure-induced Kondo volume collapse and 4f electron delocalization of Ce reduced the differences between Ce and Al and brought them within the Hume-Rothery (HR) limit for substitutional alloying. The alloy remained after complete release of pressure, which was also accompanied by the transformation of Ce back to its ambient 4f electron localized state and reversal of the Kondo volume collapse, resulting in a non-HR alloy at ambient conditions.
|
|