  • Kassamakova, L, et al. (författare)
  • Al/Si ohmic contacts to p-type 4H-SiC for power devices
  • 2000
  • Ingår i: Materials Science Forum. - 0255-5476 .- 1662-9752. ; 338-3, s. 1009-1012
  • Tidskriftsartikel (refereegranskat)abstract
    • The formation of Al/Si/p-4H SiC ohmic contacts at temperatures as low as 750 degreesC is reported in this paper. The dependence of electrical properties and contact morphology have been investigated as a function of the annealing regime in the interval 600-700 degreesC. The lowest contact resistivity of 3.8x10(-5) Omega .cm(2) was obtained at 700 degreesC annealing, however the most reproducible results were in the low 10(-4) Omega .cm(2) range. It has been established that the predominate current transport mechanism in the Al/Si/SiC contacts is thermionic-field emission. Atomic force microscopy showed that the addition of Si to the contact layer improves its morphology, and the pitting of annealed Al is not observed. The contacts developed are stable during ageing at 500 degreesC and at operating temperatures up to 450 degreesC. After the contacts testing with current density of 10(3) A/cm(2) at temperatures up to 450 degreesC, their contact resistivity decreases slightly.
  •  
Skapa referenser, mejla, bekava och länka
  • Resultat 1-2 av 2

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy