1. |
- Peruzzi, Niccolò, et al.
(author)
-
Multimodal ex vivo methods reveal that Gd-rich corrosion byproducts remain at the implant site of biodegradable Mg-Gd screws
- 2021
-
In: Acta Biomaterialia. - : Elsevier. - 1742-7061 .- 1878-7568. ; 136, s. 582-591
-
Journal article (peer-reviewed)abstract
- Extensive research is being conducted on magnesium (Mg) alloys for bone implant manufacturing, due to their biocompatibility, biodegradability and mechanical properties. Gadolinium (Gd) is among the most promising alloying elements for property control in Mg alloy implants; however, its toxicity is controversial. Investigating Gd behavior during implant corrosion is thus of utmost importance. In this study, we analyzed the degradation byproducts at the implant site of biodegradable Mg-5Gd and Mg-10Gd implants after 12 weeks healing time, using a combination of different imaging techniques: histology, energy-dispersive x-ray spectroscopy (EDX), x-ray microcomputed tomography (µCT) and neutron µCT. The main finding has been that, at the healing time in exam, the corrosion appears to have involved only the Mg component, which has been substituted by calcium and phosphorus, while the Gd remains localized at the implant site. This was observed in 2D by means of EDX maps and extended to 3D with a novel application of neutron tomography. X-ray fluorescence analysis of the main excretory organs also did not reveal any measurable accumulation of Gd, further reinforcing the conclusion that very limited or no removal at all of Gd-alloy happened during degradation.
|
|
2. |
- Wallmeier, Malte, et al.
(author)
-
Phenomenological analysis of constrained in-plane compression of paperboard using micro-computed tomography Imaging
- 2021
-
In: Nordic Pulp & Paper Research Journal. - : De Gruyter Open Ltd. - 0283-2631 .- 2000-0669. ; 36:3, s. 491-
-
Journal article (peer-reviewed)abstract
- Large deformations under in-plane compression of paperboard appear in forming processes like hydroforming, pressforming and deep drawing, but the mechanisms of deformation have not been studied on a micromechanical level. A constrained in-plane compression test is presented. This test allows for in-plane compression, buckling, wrinkling and compaction. The constrained compression test is realized using a DEBEN CT-500 in-situ tester for laboratory microtomography and synchrotron microtomography. Experiments with five different materials spanning from laboratory handsheets to commercially available multi-layered paperboards are performed. Image processing is used to observe the local out-of-plane fiber orientation and compaction. A phenomenological investigation of the deformation behavior of these materials is presented. Delamination is found to be the primary mechanisms of failure in the multi-layered boards. Furthermore, a porous network structure, created by using long and minimally refined softwood fibers, is found to facilitate the formation of uniform wrinkles and compaction.
|
|