Varestraint weldability testing of cast ATI® 718Plus™ : a comparison to cast Alloy 718

• Varestraint testing of the newly developed cast ATI® 718Plus™ after pseudo-HIP (hot isostatic pressing) heat treatments showed that the extent of solidification cracking was independent of the heat treatment condition. The susceptibility towards heat-affected zone (HAZ) liquation cracking was found to be related to the heat treatment dwell time rather than the temperature. The heat treatments at 1120 and 1190 °C for 24 h were the most susceptible to cracking. On the other hand, heat treatments at 1120, 1160 and 1190 °C for 4-h dwell time exhibited the least amount of cracking. The solidification cracking was found to be similar whereas the HAZ liquation cracking was lower for ATI® 718Plus™ after the heat treatment at 1120 and 1190 °C for 4-h dwell time in comparison to cast Alloy 718.

Subject headings

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Maskinteknik -- Teknisk mekanik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Mechanical Engineering -- Applied Mechanics (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

Keyword

Hot cracking

Cast ATI® 718Plus™

Cast alloy 718

Varestraint testing

Backfilling

Manufacturing and materials engineering

Produktions- och materialteknik

Publication and Content Type

ref (subject category)

art (subject category)