Performance of Phosphonated Hydrocarbon Ionomer in the Fuel Cell Cathode Catalyst Layer
-
- Wreland Lindström, Rakel (author)
- KTH,Tillämpad elektrokemi
-
- Oyarce, Alejandro (author)
- KTH,Tillämpad elektrokemi
-
- Aguinaga, Luis Guerrero (author)
- KTH,Tillämpad elektrokemi
-
show more...
-
- Ubeda, Diego (author)
- KTH,Tillämpad elektrokemi
-
- Ingratta, Mark (author)
- Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
-
- Jannasch, Patric (author)
- Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
-
- Lindbergh, Göran (author)
- KTH,Tillämpad elektrokemi
-
show less...
-
(creator_code:org_t)
- 2013-01-19
- 2013
- English.
-
In: Journal of the Electrochemical Society. - : The Electrochemical Society. - 0013-4651 .- 1945-7111. ; 160:3, s. F269-F277
- Related links:
-
http://jes.ecsdl.org...
-
show more...
-
http://dx.doi.org/10...
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
https://lup.lub.lu.s...
-
show less...
Abstract
Subject headings
Close
- Inexpensive and environmentally friendly electrolyte polymers that can be operated at higher temperatures and drier conditions are highly interesting for PEM fuel cells for automotive, portable power and stationary electricity generation applications. In this study an ionomer based on polysulfone grafted with poly(vinylphosphonic acid) (PSUgPVPA) in the cathode Pt/C catalyst layer was electrochemically characterized and compared to Nafion. The performance at different levels of humidity at 80 degrees C was evaluated by polarization measurements, cyclic voltammetry and electrochemical impedance spectroscopy (EIS). The results show that the performance of the PSUgPVPA-based cathode catalyst layer is comparable to that of Nafion-at 100% relative humidity (RH) but with some instabilities. However, at drier conditions significant losses of performance for the PSUgPVPA-based cathode was observed. This could be an effect of catalyst poisoning by the ionomer interfering with ORR. However, the concomitant decrease of the electrochemical surface area, double layer capacitance and increased imaginary impedance, indicate that the poorer performance at low humidity is mainly an effect of reduced catalyst wetting by the ionomer in combination with the decreased proton conduction in the ionomeric phase.
Subject headings
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering (hsv//eng)
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)
Keyword
- Gas-Diffusion Electrodes
- Mass-Transport Limitations
- Proton-Exchange Membranes
- Pefc Cathode
- Poly(Vinylphosphonic Acid)
- Intermediate Temperature
- Transient Techniques
- Relative-Humidity
- Protogenic Group
- Side-Chains
Publication and Content Type
- ref (subject category)
- art (subject category)
Find in a library
To the university's database