Sintering behaviour of the protonic conductors BaZr(x)Ce(0.8-x)Ln(0.2)O(3-delta) (x=0.8, 0.5, 0.1; Ln=Y, Sm, Gd, Dy) during the solid-state reactive-sintering process
-
- Bu, Junfu (författare)
- KTH,Tillämpad processmetallurgi
-
- Jönsson, Pär G. (författare)
- KTH,Tillämpad processmetallurgi
-
- Zhao, Zhe (författare)
- KTH,Tillämpad processmetallurgi,Shanghai Institute of Technology, China
-
(creator_code:org_t)
- Elsevier BV, 2015
- 2015
- Engelska.
-
Ingår i: Ceramics International. - : Elsevier BV. - 0272-8842 .- 1873-3956. ; 41:2, s. 2558-2564
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- The protonic conductors BaZr(x)Ce(0.8-x)Ln(0.2)O(3-delta) (x=0.8, 0.5, 0.1; Ln=Y, Sm, Gd, Dy) were successfully prepared using a solid-state reactive-sintering method. NiO (1 wt.%) was added as a sintering aid, and it was proven that NiO produced tremendous enhancement in the densification process. The morphologies of the variously doped BaZr(0.8)Ln(0.2)O(3-delta), BaZr(0.5)Ce(0.3)Ln(0.2)O(3-delta) and BaZr(0.1)Ce(0.7)Ln(0.2)O(3-delta) ceramics, as well as their sintering behaviour, were investigated. The results show that the Ce content in the BaZr(0.8)Ln(0.2)O(3-delta), BaZr(0.5)Ce(0.3)Ln(0.2)O(3-delta) and BaZr(0.1)Ce(0.7)Ln(0.2)O(3-delta) compounds influences the sintering temperature significantly, and a larger Ce content will lead to a lower sintering temperature. In addition, ionic radii of the dopants that are similar to the ionic radii of the B-site will also result in a lowered sintering temperature. Based on the present study, NiO has no influence on the lattice parameters.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
Nyckelord
- Solid state reaction
- Milling
- Sintering
- Fuel cells
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas