- Article/chapterEnglish2016
Publisher, publication year, extent ...
-
2016-05-09
-
Springer,2016
-
printrdacarrier
Numbers
-
LIBRIS-ID:oai:DiVA.org:kth-189908
-
https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-189908URI
-
https://doi.org/10.1007/s11664-016-4579-1DOI
Supplementary language notes
-
Language:English
-
Summary in:English
Part of subdatabase
Classification
-
Subject category:ref swepub-contenttype
-
Subject category:art swepub-publicationtype
Notes
-
QC 20160808
-
Ruthenium is the most promising material for the barrier layer used for the sub 14 nm technology node in integrated circuits manufacturing. Potassium periodate (KIO4)-based slurry is used in the chemical mechanical planarization (CMP) process of the barrier layer. However, the electrochemical and corrosion properties of ruthenium have not been investigated in such slurry. In this paper, the electrochemical and corrosion behaviors of ruthenium in KIO4 solutions were investigated under static conditions but at different pH values by potentiodynamic polarization and electrochemical impedance spectroscopy measurements, combined with surface chemical analysis using auger electron spectroscopy. Moreover, to study wear enhanced corrosion during CMP, tribocorrosion experiments were carried out to monitor the current density changes during and after mechanical scratching. The results show that at pH 6, ruthenium forms a relatively thick and heterogeneous surface film composed of RuO2 center dot 2H(2)O/RuO3, showing a high corrosion resistance and it exhibits a quick repassivation after mechanical scratching. At pH 4, ruthenium shows a passivation behavior with formation of a uniform and conductive oxide like RuO2 center dot 2H(2)O. It should be noted that there is a possible formation of RuO4 toxic gas under this condition, which should be avoided in the actual production. However, at pH 11, ruthenium exhibits no considerable passivity and the corrosion proceeds uniformly.
Subject headings and genre
Added entries (persons, corporate bodies, meetings, titles ...)
-
Wang, Tongqing
(author)
-
Pan, JinshanKTH,Yt- och korrosionsvetenskap(Swepub:kth)u17ks6cf
(author)
-
Lu, Xinchun
(author)
-
KTHYt- och korrosionsvetenskap
(creator_code:org_t)
Related titles
-
In:Journal of Electronic Materials: Springer45:8, s. 4067-40750361-52351543-186X
Internet link
Find in a library
To the university's database