Ferroelectric and colossal magnetoresistive properties of a PbZr1-xTixO3/La1-xSrxMnO3 heterostructure film
-
Mitsugi, F. (author)
-
Yamagata, Y. (author)
-
Ikegami, T. (author)
-
show more...
-
Ebihara, K. (author)
-
Narayan, J. (author)
-
- Grishin, Alexander M. (author)
- KTH,Mikroelektronik och informationsteknik, IMIT
-
show less...
-
(creator_code:org_t)
- 2000
- 2000
- English.
-
In: Japanese Journal of Applied Physics. - 0021-4922 .- 1347-4065. ; 39:9B, s. 5418-5420
- Related links:
-
https://urn.kb.se/re...
-
show more...
-
https://doi.org/10.1...
-
show less...
Abstract
Subject headings
Close
- We report the ferroelectric and magnetoresistive properties and crystallization of a PbZr0.52Ti0.48O3 (PZT)/La0.8Sr0.2MnO3 (LSMO) heterostructure film prepared by pulsed-laser deposition on a MgO(100) single crystal substrate. Ferroelectric properties such as the hysteresis loop and dielectric constant of the Au/PZT/LSMO capacitor were compared with those of the Au/PZT/YBa2Cu3O7-x, (YBCO) superconductor heterostructure film. The resistivity of the LSMO film was as low as that of the YBCO film at room temperature. The fabricated Au/PZT/LSMO capacitor had a remanent polarization of 29 muC/cm(2), a coercive field of 30 kV/cm and a dielectric constant of about 1000.
Keyword
- PZT
- LSMO
- ferroelectrics
- colossal magnetoresistance
- heterostructure
- pulsed-laser deposition
- thin-films