La0.1SrxCa0.9-xMnO3-δ -Sm0.2Ce0.8O1.9 composite material for novel low temperature solid oxide fuel cells
-
- Wang, Xunying (författare)
- Hubei University Wuhan, China
-
- Afzal, Muhammad (författare)
- KTH,Energiteknik
-
- Deng, Hui (författare)
- Hubei University Wuhan, China
-
visa fler...
-
- Dong, Wenjing (författare)
- Hubei University Wuhan, China
-
- Wang, Baoyuan (författare)
- Hubei University Wuhan, China
-
- Mi, Youquan (författare)
- Hubei University Wuhan, China
-
- Xu, Zhaoyun (författare)
- Hubei University Wuhan, China
-
- Zhang, Wei (författare)
- Hubei University Wuhan, China
-
- Feng, Chu (författare)
- Hubei University Wuhan, China
-
- Wang, Zhaoqing (författare)
- Hubei University Wuhan, China
-
- Wu, Yan (författare)
- China University of Geosciences Wuhan, China
-
- Zhu, Bin (författare)
- KTH,Kraft- och värmeteknologi
-
visa färre...
-
(creator_code:org_t)
- Elsevier, 2017
- 2017
- Engelska.
-
Ingår i: International journal of hydrogen energy. - : Elsevier. - 0360-3199 .- 1879-3487. ; 42:27, s. 17552-17558
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Lowering the operating temperature of the solid oxide fuel cells (SOFCs) is one of the world R&D tendencies. Exploring novel electrolytes possessing high ionic conductivity at low temperature becomes extremely important with the increasing demands of the energy conversion technologies. In this work, perovskite La0.1SrxCa0.9-xMnO3-δ (LSCM) materials were synthesized and composited with the ionic conductor Sm0.2Ce0.8O1.9 (SDC). The LSCM-SDC composite was sandwiched between two nickel foams coated with semiconductorNi0.8Co0.15Al0.05LiO2- δ (NCAL) to form the fuel cell device. The strontium content in theLSCM and the ratios of LSCM to SDC in the LSCM-SDC composite have significant effects on the electrical properties and fuel cell performances. The best performance has been achieved from LSCM-SDC composite with a weight ratio of 2:3. The fuel cells showed OCV over 1.0 V and excellent maximum output power density of 800 mW/cm2 at 550 ºC. Device processes and ionic transport processes were also discussed.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Keramteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Ceramics (hsv//eng)
Nyckelord
- Perovskite ionic-conductor; composite material; Electrolyte; Low temperature SOFCs
- Energiteknik
- Energy Technology
- Materials Science and Engineering
- Teknisk materialvetenskap
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Wang, Xunying
-
Afzal, Muhammad
-
Deng, Hui
-
Dong, Wenjing
-
Wang, Baoyuan
-
Mi, Youquan
-
visa fler...
-
Xu, Zhaoyun
-
Zhang, Wei
-
Feng, Chu
-
Wang, Zhaoqing
-
Wu, Yan
-
Zhu, Bin
-
visa färre...
- Om ämnet
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Materialteknik
-
och Keramteknik
- Artiklar i publikationen
-
International jo ...
- Av lärosätet
-
Kungliga Tekniska Högskolan