MoO3 Evaporation Studies from Binary Systems towards Choice of Mo Precursors in EAF
- Article/chapterEnglish2010
Publisher, publication year, extent ...
-
2010-08-20
-
Wiley,2010
-
printrdacarrier
Numbers
-
LIBRIS-ID:oai:DiVA.org:kth-24516
-
https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-24516URI
-
https://doi.org/10.1002/srin.201000055DOI
Supplementary language notes
-
Language:English
-
Summary in:English
Part of subdatabase
Classification
-
Subject category:ref swepub-contenttype
-
Subject category:art swepub-publicationtype
Notes
-
QC 20100913. Uppdaterad från in press till published (20101203).
-
The evaporation rate of molybdenum oxide from mixtures with CaO or MgO was studied in the temperature range 300-1573 K. The investigations were carried out using high temperature X-ray diffraction and thermogravimetry. Further, additions of these precursors to molten steel in the laboratory scale and the Mo yield achieved were determined. The X-ray studies show that the calcium molybdate is formed from the oxide mixture in the temperature interval 773-873K, which precedes the beginning of evaporation of MoO3. Results of thermogravimetric studies with mixtures CaO and MgO with MoO3 as well as the compounds CaMoO4 and MgMoO4 confirm the above results. Addition of various molybdenum precursors, viz, the mixtures of carbon with pure MoO3, CaMoO4 and MgMoO4, as well as oxide mixtures (CaO + MoO3, MgO + MoO3) show that the highest yield was observed for CaMoO4 + C and MoO3 + C mixtures, while MgO + C + MoO3 mixture showed much lower yield.
Subject headings and genre
Added entries (persons, corporate bodies, meetings, titles ...)
-
Teng, LidongKTH,Materialens processvetenskap(Swepub:kth)u1cd4hn6
(author)
-
Seetharaman, SeshadriKTH,Materialens processvetenskap(Swepub:kth)u1dt6m1e
(author)
-
KTHMaterialens processvetenskap
(creator_code:org_t)
Related titles
-
In:Steel Research International: Wiley81:9, s. 784-7911611-3683
Internet link
Find in a library
To the university's database