Stacking fault energy and deformation behaviour of austenitic stainless steels: a joint theoretical-experimental study

Molnár, Dávid Sándor, 1990- (author)
Högskolan Dalarna,KTH,Tillämpad materialfysik,Materialteknik,KTH, Tillämpad materialfysik
Vitos, Levente, Prof. (thesis advisor)
KTH,Materialvetenskap,Tillämpad materialfysik,Tillämpad fysik,KTH, Materialvetenskap
Engberg, Göran (thesis advisor)
Högskolan Dalarna,Materialteknik
show more...
Chai, Guocai (opponent)
show less...
 (creator_code:org_t)
ISBN 9789178733163
Stockholm : KTH Royal Institute of Technology, 2019
English 80 s.
Series: TRITA-ITM-AVL ; 2019:33
  • Doctoral thesis (other academic/artistic)
Abstract Subject headings
Close  
  • Austenitiska rostfria stål är främst kända för sin exceptionella korrosionsbeständighet. De har en ytcentrerad kubisk (FCC) struktur som stabiliseras genom att nickel, mangan eller kväve tillsätts till Fe-Cr legeringen. Fe-Cr-Ni-systemet kan utökas ytterligare genom tillsats av andra element såsom Mo, Cu, Ti, C, etc. för att förbättra egenskaperna. Eftersom austenitiska rostfria stål ofta används som konstruktionsmaterial är det viktigt att kunna förutsäga deras mekaniska egenskaper baserat på deras sammansättning, mikrostruktur, magnetiska tillstånd, etc. I denna avhandling är det plastiska deformationsbeteendet hos austenitiska rostfria stål undersökt med teoretiskt och experimentellt. I FCC material spelar staplingsfelsenergin (SFE) en viktig roll vid förutsägelsen och beskrivning av deformationsmekanism. Baserat på storleken av SFE kan olika deformationsmekanismer observeras, såsom martensitbildning, tvillingbildning, eller dislokationsglidning. Alla dessa funktioner påverkar beteendet, därför är det önskvärt att förutsäga och kontrollera deras förekomst. Legering och temperatur har stark inverkan på SFE och därmed legeringarnas mekaniska egenskaper. Flera modeller, baserade på SFE och mer nyligen på den så kallade generaliserade staplingsfelenergin (GSFE eller γ-surface), är tillgängliga för att förutsäga legeringens affinitet till tvillingbildning och den kritiska spänning som representerar den minsta upplösta skjuvspänningen som krävs för att initiera tvillingbildning. Man kan använda ab initio beräkningar baserade på täthetsfunktionalteori (DFT) för att beräkna GSFE för austenitiska stål och härleda parametrar som twinnability och kritisk tvillingsspänning.Korrelation mellan staplingsfelenergi och deformationsbeteendet för fyra olika austenitiska rostavstavning stål diskuteras i detta arbete. SFE för de valda legeringarna erhålls genom ab initio beräkningar och baserat på olika modeller, deras tendens till tvillingbildning och den kritiska tvillingsspänningen kan förutsägas. Deras mekaniska beteende och affinitet till tvilling och martensitisk transformation kartläggs över ett brett temperaturområde (−70°C to +500°C) för de fyra legeringarna. De teoretiska förutsägelserna jämförs med resultat från dragprov och bakåtspridd elektrondiffraktion (EBSD). Flera konventionella och in situ dragprov utfördes för att verifiera de teoretiska resultaten. Vi utförde EBSD-mätningar på dragprov som avbrutits vid olika töjningar och efter brott samt med in situ dragprov för att följa utvecklingen av mikrostrukturen noggrant. Vi tar hänsyn till de inre energibarriärernas roll i våra förutsägelser och presenterar ett nytt sätt att experimentellt få GSFE av austenitiska rostfria stål. Tidigare kunde endast SFE mätas tillförlitligt genom väl utformade experiment. I den aktuella avhandlingen går vi vidare och föreslår en teknik som kan ge noggranna värden för den instabila staplingsfelenergin för alla austenitiska legeringar som uppvisar tvillingbildning på låga spänningsnivåer. Betydelsen av temperatur och mellanliggande legering på mekaniskt beteende undersökt också i detta arbete.
  • Austenitic stainless steels are primarily known for their exceptional corrosion resistance. They have the face centred cubic (FCC) structure which is stabilised by adding nickel, manganese or nitrogen to the Fe-Cr alloy. The Fe-Cr-Ni system can be further extended by adding other elements such as Mo, Cu, Ti, C, etc. to improve the properties. Since austenitic stainless steels are often used as structural materials, it is important to be able to predict their mechanical behaviour based on their composition, microstructure, magnetic state, etc.In this work, the plastic deformation behaviour of austenitic stainless steels is investigated by theoretical and experimental approaches. In FCC materials the stacking fault energy (SFE) plays an important role in the description and prediction of the deformation modes. Based on the magnitude of the SFE different deformation modes can be observed such as martensite formation, deformation twinning, or dislocation glide. All these deformation modes influence the material behaviour, therefore it is desired to predict and control their occurrence. Alloying elements and temperature have a strong effect on the SFE and thus on the mechanical properties of the alloys. Several models based on the SFE and more recently on the so-called generalised stacking fault energy (GSFE or γ-surface) are available to describe the alloy's affinity to twinning and the critical twinning stress representing the minimum resolved shear stress required to initiate the deformation twinning mechanism. One can employ well established experimental techniques to measure the SFE. On the other hand, one needs to resort to ab initio calculations based on density functional theory (DFT) to compute the GSFE of austenitic steels and derive parameters like the twinnability and the critical twinning stress.The correlation between the stacking fault energy and the deformation behaviour for four different austenitic stainless steels is discussed in this work. The SFE of the selected alloys is obtained by ab initio calculations and based on different models, their tendency for twinning and their critical twinning stress is predicted. The mechanical behaviour and the affinity for twinning and martensitic transformation is mapped across a broad range of temperature (-70°C to +500°C) for the four alloys. The theoretical predictions are contrasted with tensile tests and electron backscatter diffraction (EBSD) measurements. Several conventional and in situ tensile test are performed to verify the theoretical results. EBSD measurements on interrupted and fractured specimens, and during in situ tensile tests were carried out to closely follow the development of the microstructure. In the present thesis, a technique is proposed that can provide accurate unstable stacking fault energy values for any austenitic alloy exhibiting twinning at low stress values. The importance of temperature and interstitial alloying on mechanical behaviour is also investigated.

Subject headings

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

Keyword

austenitic stainless steel
deformation properties
stacking fault energy
electron backscatter diffraction
ab initio
Teknisk materialvetenskap
Materials Science and Engineering
Steel Forming and Surface Engineering

Publication and Content Type

vet (subject category)
dok (subject category)

Find in a library

To the university's database

  • 1 of 1
  • Previous record
  • Next record
  •    To hitlist

Find more in SwePub

By the author/editor
Molnár, Dávid Sá ...
Vitos, Levente, ...
Engberg, Göran
Chai, Guocai
About the subject
ENGINEERING AND TECHNOLOGY
ENGINEERING AND ...
and Materials Engine ...
and Metallurgy and M ...
Parts in the series
By the university
Royal Institute of Technology
Högskolan Dalarna

Search outside SwePub

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Close

Copy and save the link in order to return to this view