Effective X-ray Elastic Constant of Cast Iron
- Article/chapterEnglish2018
Publisher, publication year, extent ...
-
2017-10-12
-
Springer Science and Business Media LLC,2018
-
electronicrdacarrier
Numbers
-
LIBRIS-ID:oai:DiVA.org:liu-141980
-
https://urn.kb.se/resolve?urn=urn:nbn:se:liu:diva-141980URI
-
https://doi.org/10.1007/s10853-017-1657-6DOI
Supplementary language notes
-
Language:English
-
Summary in:English
Part of subdatabase
Classification
-
Subject category:ref swepub-contenttype
-
Subject category:art swepub-publicationtype
Notes
-
Funding agencies: Agora Materiae, graduate school, the Swedish Government Strategic Research Area in Materials Science on Functional Materials at Linkoping University [2009-00971]; Volvo Trucks; Vinnova FFI, Scania
-
X-ray diffraction is a non-destructive method used for strain measurements in crystalline materials. Conversion of strain to stress can be achieved using the X-ray elastic constants (XEC), s1 and ½s2. The sin2ψ method was used during in situ loading to determine XEC for flake, vermicular, and spherical graphite iron. A fully pearlitic steel was used as reference. Uniaxial testing was conducted on the cast iron to create a homogeneous strain field, as well as four-point bending in both tension and compression due to the tension/compression asymmetry. The commonly used XEC value ½s2 = 5.81 × 10−6 MPa−1 is theoretically derived from an α-Fe single crystal. When investigating materials that contain ferrite, such as polycrystalline cast iron, this value is not accurate. Determination of an effective XEC for polycrystalline cast iron yields a better correlation between the measured microstrains and the properties observed on a macroscopic scale. The need for an effective XEC is evident, especially when it comes to model validation of, for example, casting simulations. Effective XEC values have been determined for flake, vermicular, and spherical graphite iron. The determined value is lower than the theoretical value.
Subject headings and genre
Added entries (persons, corporate bodies, meetings, titles ...)
-
Saarimäki, Jonas,1985-Linköpings universitet,Konstruktionsmaterial,Tekniska fakulteten(Swepub:liu)jonsa20
(author)
-
Moverare, Johan,1973-Linköpings universitet,Konstruktionsmaterial,Tekniska fakulteten(Swepub:liu)johmo31
(author)
-
Peng, Ru Lin,1960-Linköpings universitet,Konstruktionsmaterial,Tekniska fakulteten(Swepub:liu)rupe37
(author)
-
Linköpings universitetKonstruktionsmaterial
(creator_code:org_t)
Related titles
-
In:Journal of Materials Science: Springer Science and Business Media LLC53:4, s. 2766-27730022-24611573-4803
Internet link
Find in a library
To the university's database