Microstructural Evolution During High Temperature Dwell-fatigue of Austenitic Stainless Steels

Wärner, Hugo,1988-Linköpings universitet,Konstruktionsmaterial,Tekniska fakulteten (författare)

Funding agencies: AB Sandvik Materials Technology in Sweden; Swedish Energy Agency through the Research Consortium of Materials Technology for Thermal Energy Processes [KME-701]
Microstructural evolution related to the mechanical response from isothermal dwell-fatigue testing at 700 °C of two austenitic steels, Esshete 1250 and Sanicro 25, is reported. Coherent Cu-precipitates and incoherent Nb-carbides were found to impede dislocation motion, increase hardening and improving the high temperature properties of Sanicro 25. Sparsely placed intergranular Cr- and Nb-carbides made Esshete 1250 susceptible to creep damage and intergranular crack propagation, mainly from interaction of the carbides and fatigue induced slip bands. Dynamic recrystallization of the plastic zone at the crack tip appeared to affect crack propagation of Sanicro 25 by providing an energetically privileged path.

Xu, JinghaoLinköpings universitet,Konstruktionsmaterial,Tekniska fakulteten(Swepub:liu)jinxu03 (författare)
Chai, Guocai,1956-Linköpings universitet,Konstruktionsmaterial,Tekniska fakulteten,Sandvik Materials Technology, Sandviken(Swepub:liu)guoch17 (författare)
Moverare, Johan,1973-Linköpings universitet,Konstruktionsmaterial,Tekniska fakulteten(Swepub:liu)johmo31 (författare)
Calmunger, Mattias,1986-Linköpings universitet,Konstruktionsmaterial,Tekniska fakulteten(Swepub:liu)mathu54 (författare)
Linköpings universitetKonstruktionsmaterial (creator_code:org_t)

Av författaren/redakt...: Wärner, Hugo, 19 ...; Xu, Jinghao; Chai, Guocai, 19 ...; Moverare, Johan, ...; Calmunger, Matti ...

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.