Thermoelectric Characteristics of Self-Supporting WSe2-Nanosheet/PEDOT-Nanowire Composite Films

• Conducting polymer poly(3,4-ethylenedioxythiophene) nanowires(PEDOTNWs) were synthesized by a modified self-assembled micellar soft-templatemethod, followed by fabrication by vacuum filtration of self-supportingexfoliated WSe2-nanosheet (NS)/PEDOT-NW composite films.The results showed that as the mass fractions of WSe2 NSsincreased from 0 to 20 wt % in the composite films, the electricalconductivity of the samples decreased from & SIM;1700 to & SIM;400S cm(-1), and the Seebeck coefficient increased from12.3 to 23.1 & mu;V K-1 at 300 K. A room-temperaturepower factor of 44.5 & mu;W m(-1) K-2 was achieved at 300 K for the sample containing 5 wt % WSe2 NSs, and a power factor of 67.3 & mu;W m(-1) K-2 was obtained at 380 K. The composite film containing5 wt % WSe2 NSs was mechanically flexible, as shown byits resistance change ratio of 7.1% after bending for 500 cycles ata bending radius of 4 mm. A flexible thermoelectric (TE) power generatorcontaining four TE legs could generate an output power of 52.1 nWat a temperature difference of 28.5 K, corresponding to a power densityof & SIM;0.33 W/m(2). This work demonstrates that the fabricationof inorganic nanosheet/organic nanowire TE composites is an approachto improve the TE properties of conducting polymers.

Subject headings

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Textil-, gummi- och polymermaterial (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Textile, Rubber and Polymeric Materials (hsv//eng)

Keyword

thermoelectric; composite; WSe2; conducting polymer; flexibility

Publication and Content Type

ref (subject category)

art (subject category)