Macrodefects in cubic silicon carbide crystals

• Different sublimation growth conditions of 3C-SiC approaching a bulk process have been investigated with the focus on appearance of macrodefects. The growth rate of 3C-SiC crystals grown on 6H-SiC varied from 380 to 460 mu m/h with the thickness of the crystals from 190 to 230 mu m, respectively. The formation of macrodefects with void character was revealed at the early stage of 3C-SiC crystal growth. The highest concentration of macrodefects appears in the vicinity of the domain in samples grown under high temperature gradient: and fastest temperature ramp up. The formation of macrodefects was related to carbon deficiency which appear due to high Si/C ratio which is used to enable formation of the 3C-SiC polytype.

Keyword

3C-SiC crystals; sublimation epitaxy; voids