Interface chemistry of WN/4H-SiC structures

• The interface chemistry of WN/4H–SiC structures has been studied by means of X-ray photoelectron spectroscopy (XPS). XPS investigations have been performed on as deposited, 800°C and 1200°C annealed (4 min) samples. The as deposited and 800°C annealed samples are characterized by chemically inert interfaces. Complete nitrogen out-diffusion from the WN layer, significant carbon diffusion into the contact layer, tungsten carbide and tungsten silicide formation occur during the 1200°C annealing process. The 800°C annealed WN/4H–SiC contacts are found to be of a Schottky type with a barrier height of 0.91 eV. The Schottky barrier height and the ideality factor show no significant changes during 100 h storage at 500°C under nitrogen and during operation at increasing temperature up to 350°C in air.

Nyckelord

Depth profiling; Electrical properties and measurements; Tungsten nitride; Silicon carbide