Creep Fracture Mechanism of Polycrystalline Ni-based Superalloy with Diffusion Coatings
-
- Yuan, Kang (author)
- Linköpings universitet,Konstruktionsmaterial,Tekniska högskolan
-
- Peng, Ru (author)
- Linköpings universitet,Konstruktionsmaterial,Tekniska högskolan
-
- Li, Xin-Hai (author)
- Siemens Industrial Turbomachinery AB, Finspång
-
show more...
-
- Johansson, Lennart (author)
- Siemens Industrial Turbomachinery AB, Finspång
-
- Johansson, Sten (author)
- Linköpings universitet,Konstruktionsmaterial,Tekniska högskolan
-
- Wang, Yandong (author)
- School of Materials Science and Engineering, Beijing Institute of Technology, Beijing, China
-
show less...
-
(creator_code:org_t)
- 2013
- 2013
- English.
- Related links:
-
https://urn.kb.se/re...
Abstract
Subject headings
Close
- Diffusion coatings are widely used to increase oxidation and corrosion resistance of hot superalloy components for gas turbines. The aim of this study is to investigate the effect of coatings (NiAl and PtAl) on the creep fracture mechanism of samples with a substrate of IN792. The samples have been creep tested at two temperatures (850 °C and 950 °C) and different applied tensile stresses, until failure between 205 and 21000 hrs. The observation of cross-sections by SEM shows that the microstructural evolution in the coating is dependent on the diffusion of alloying elements in the sample. Furthermore the time and temperature induced growth of the coating is found to be controlled only by inward diffusion of Al. Grain-boundary cracking is the basic fracture mode in the substrate in all samples irrespective if the crack is initiated from coating or substrate. The analysis of microstructure shows that the diffusion coatings display two types of mechanical behavior - being easily plasticized or cracked - dependent on temperature and type of coating, and therefore can be considered as non-load carrying regions. After recalculating the creep stress to exclude the final effective coating thickness from the total sample thickness, the coated samples showed similar creep rupture behavior as the uncoated samples in the Larson-Miller diagram.
Subject headings
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
Keyword
- Creep; Ni-based superalloy; Diffusion coating; Crack