Enhanced Performance and Stability in Polymer Photovoltaic Cells Using Ultraviolet-Treated PEDOT:PSS

• We investigate the effects of ultraviolet (UV) irradiation treatment with varying irradiation intensities for different treatment times of poly(3, 4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) film on the performance and stability of polymer solar cells (PSCs) based on regioregular poly(3-hexylthiophene) (P3HT) and methanofullerene [6,6]-phenyl C-61-butyric acid methyl ester (PCBM) blend. Ultraviolet-visible transmission spectra, x-ray photoelectron spectroscopy, contact angle measurement, atomic force microscopy and the Kelvin probe method are conducted to characterize the UV-treated PEDOT:PSS film. The results demonstrate that UV treatment can improve the power conversion efficiency (PCE) and stability of PSCs effectively. The best performance is achieved under 1200 mu W/cm(2) UV treatment for 50 min. Compared to the control device, the optimized device exhibits enhanced performance with a V-OC of 0.59 V, J(SC) of 12.3 mA/cm(2), fill factor of 51%, and PCE of 3.64%, increased by 3.5%, 33%, 8.7% and 50%, respectively. The stability of the PSCs is enhanced by 2.5 times simply through the UV treatment on the PEDOT:PSS buffer layer. The improvement in the device performance and stability is attributed to the improvement in the wettability property and the increase in the work function of the PEDOT:PSS film by UV treatment, while the impact of UV treatment on the transparency of the PEDOT:PSS film is negligible. The strategy of using UV treatment to improve device performance and stability is attractive due to its simplicity, cost-effectiveness, and because it is suitable for large-scale commercial production.

Keyword

TECHNOLOGY

TEKNIKVETENSKAP

Publication and Content Type

ref (subject category)

art (subject category)