Effect of Ni conten...
-
Irshad, Hafiz MusammilKing Fahd University of Petroleum & Minerals, Saudi Arabia
(författare)
Effect of Ni content and Al2O3 particle size on the thermal and mechanical properties of Al2O3/Ni composites prepared by spark plasma sintering
- Artikel/kapitelEngelska2018
Förlag, utgivningsår, omfång ...
-
Elsevier,2018
-
printrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:lnu-75655
-
https://urn.kb.se/resolve?urn=urn:nbn:se:lnu:diva-75655URI
-
https://doi.org/10.1016/j.ijrmhm.2018.05.010DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
Alumina-nickel composites were prepared by carrying out spark plasma sintering (SPS) of nano-sized and micro-sized Al2O3particles with 15–45 wt% Ni powders. The powder materials were sintered at a temperature of1400 °C under a constant uniaxial pressure of 50 MPa. FESEM micrographs of the products showed uniformlydispersed nickel inclusions in both matrices at intergranular positions. Presence of Al2O3as the major phasealong with Ni as the minor phase was confirmed using XRD analysis. Thermal and mechanical properties of thenano- and micro-sized Al2O3/Ni composites were investigated. The thermal conductivity of nano-sized aluminacomposites was seen to increase with the increase in nickel content, however, an opposite trend was observed formicro-sized alumina-based composites. Moreover, thermal conductivities of all the composites decreased withincrease in temperature. The composites also showed high hardness and fracture toughness values of up to19.6 GPa and 4.71 MPa ∗ m1/2, respectively, and relative density values, between 79 and 99%, that decreasedwith increasing Ni content. Furthermore, the nano-sized Al2O3/Ni composites showed thermal and mechanicalproperties superior to those of the micro-sized Al2O3/Ni composite.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Hakeem, Abbas SaeedKing Fahd University of Petroleum & Minerals, Saudi Arabia
(författare)
-
Ahmed, Bilal AnjumKing Fahd University of Petroleum & Minerals, Saudi Arabia
(författare)
-
Ali, Sharafat,1976-Linnéuniversitetet,Institutionen för byggd miljö och energiteknik (BET),Glass group(Swepub:lnu)salkem
(författare)
-
Ali, SadaqatImam Abdulrahman bin Faisal University, Saudi Arabia
(författare)
-
Ali, SameerUniversity of Gujrat, Pakistan
(författare)
-
Ehsan, Muhammad AliKing Fahd University of Petroleum & Minerals, Saudi Arabia
(författare)
-
Laoui, TaharKing Fahd University of Petroleum & Minerals, Saudi Arabia
(författare)
-
King Fahd University of Petroleum & Minerals, Saudi ArabiaInstitutionen för byggd miljö och energiteknik (BET)
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:International journal of refractory metals & hard materials: Elsevier76, s. 25-320263-4368
Internetlänk
Hitta via bibliotek
Till lärosätets databas