Thermoplastic polymer impregnation of cellulose nanofibre networks : Morphology, mechanical and optical properties

• Biobased nanocomposite sheets of cellulose nanofibres (CNF) and cellulose acetate butyrate (CAB) were prepared using a resin impregnation technique. Porous nanofibre networks together with a low viscosity thermoplastic resin were the key elements in the processing. SEM images of the network before the impregnation showed high porosity and after the impregnation indicated impregnated fibre network. A significant improvement in the visible light transmittance was observed for the nanocomposite compared to the nanofibre network, which is explained on the filling of the pores with a transparent matrix. The tensile tests showed an increase of 364% and 145% for stiffness and strength respectively for nanocomposites with 60 wt.% CNF when compared to CAB. Dynamic mechanical properties showed a good interaction between the CAB and cellulose nanofibres. These results show that CAB impregnated cellulose nanofibre networks are promising biocomposite that could be used in applications where transparency and good mechanical properties are of interest.

Subject headings

TEKNIK OCH TEKNOLOGIER  -- Industriell bioteknik -- Biomaterial (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Industrial Biotechnology -- Bio Materials (hsv//eng)

Keyword

Trä och bionanokompositer

Wood and Bionanocomposites

Publication and Content Type

ref (subject category)

art (subject category)